Cavitation erosion resistance of a-C:H coatings produced by PECVD on stainless steel and NiTi substrates

被引：18

作者：

Gerke, L. ^{[1
]}

Stella, J. ^{[2
]}

Schauer, J-C ^{[3
]}

Pohl, M. ^{[1
]}

Winter, J. ^{[3
]}

机构：

[1] Ruhr Univ Bochum, Chair Mat Testing, Fac Mech Engn, D-44780 Bochum, Germany

[2] Univ Simon Bolivar, Dept Ciencias Mat, Caracas 1080, Venezuela

[3] Ruhr Univ Bochum, Inst Expt Phys 2, Fac Phys & Astron, D-44780 Bochum, Germany

来源：

SURFACE & COATINGS TECHNOLOGY | 2010年 / 204卷 / 21-22期

关键词：

DLC coatings; PECVD; NiTi; Stainless steel; Cavitation erosion; DLC COATINGS; CARBON; FILMS;

D O I：

10.1016/j.surfcoat.2010.04.003

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The resistance against cavitation erosion of hydrogenated a-C:H coated materials coated by PECVD process has been evaluated. Coatings of thicknesses between 50 and 300 nm were deposited on a pseudoelastic NiTi and two stainless steel substrates and were tested by vibratory cavitation. The results show that the incubation periods of the tested coatings deposited on steel substrates were differently modified as the coating thickness was increased depending on the type of steel substrate. On the other hand, a-C:H coatings below a critical thickness deposited on pseudoelastic NiTi exhibit an excellent resistance against cavitation erosion. The outstanding results observed in a-C:H coatings deposited on NiTi are attributed to the coating capability of copying the reversible deformation that takes place in the metallic substrate combined with a strong adhesive connection. Based on the above results, a promising application potential of a-C:H on pseudoelastic shape memory substrates is expected. (C) 2010 Elsevier B.V. All rights reserved.

引用

页码：3418 / 3424

页数：7

共 20 条

[1] Cavitation erosion resistance of heat-treated NiTi [J].

Cheng, FT ;

Shi, P ;

Man, HC .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 339 (1-2) :312-317

[2] Correlation of cavitation erosion resistance with indentation-derived properties for a NiTi alloy [J].

Cheng, FT ;

Shi, P ;

Man, HC .

SCRIPTA MATERIALIA, 2001, 45 (09) :1083-1089

[3] Micro-and nanostructured diamond films under wear charging in cavitation test [J].

Deuerler, F ;

Pohl, M ;

Hessing, C .

SURFACE & COATINGS TECHNOLOGY, 2003, 174 :732-737

[4]

FEYER M, 1995, WERKSTOFFCHARAKTERIS

[5] Adhesion and elasticity of plasma deposited wear resistant a-C:H coatings on nickel-titanium [J].

Gerke, Lorenz ;

Schauer, Janine-Christina ;

Pohl, Michael ;

Winter, Joerg .

SURFACE & COATINGS TECHNOLOGY, 2009, 203 (20-21) :3214-3218

[6] Diamond-like carbon coatings as biocompatible materials - an overview [J].

Grill, A .

[7] INTERFACE MODIFICATIONS FOR IMPROVING THE ADHESION OF ALPHA-C-H FILMS TO METALS [J].

GRILL, A ;

MEYERSON, B ;

PATEL, V .

JOURNAL OF MATERIALS RESEARCH, 1988, 3 (02) :214-218

[8] A review of modified DLC coatings for biological applications [J].

Hauert, R .

[9] DLC coatings: Effects of physical and chemical properties on biological response [J].

Ma, Wen J. ;

Ruys, Andrew J. ;

Mason, Rebecca S. ;

Martin, Phil J. ;

Bendavid, Avi ;

Liu, Zongwen ;

Ionescu, Mihail ;

Zreiqat, Hala .

BIOMATERIALS, 2007, 28 (09) :1620-1628

[10]

MIYAKE S, 1992, DIAMOND FILM TECHNOL, V1, P205

← 1 2 →