Interfilament Resistance at 77 K in Striated HTS Coated Conductors

Striating HTS coated conductor (CC) tapes into narrow filaments offers the possibility of reducing the tapes' magnetization losses without unreasonably decreasing their currentcarrying capability. However, realizing well-separated striations presents technological challenges, especially if the number of filaments is large and/or if a thick layer of metallic stabilizer is present. In these situations, the filaments can be easily coupled and their effectiveness to reduce magnetization losses is strongly diminished or eliminated. While the onset of coupling is well visible from magnetization loss measurements, the actual path of the coupling current is unknown. In this contribution, we present a systematic study of the transverse resistance in HTS CC samples in order to get a deeper understanding of those paths. The measured samples differ in terms of manufacturer (SuperPower and SuperOx), and presence and thickness of stabilizer material. In addition, oxidation is used as a means to increase the resistance between the filaments in nonstabilized samples. The results are interpreted with a chain network model. This study provides useful insights on the factors determining the transverse resistance in striated HTS CCs, thus indicating ways to improve the effectiveness of the striation process for ac loss reduction.