Influence of thermal stabilization treatment on microstructure evolution of the mushy zone and subsequent directional solidification in Ti-43Al-3Si alloy

被引：16

作者：

Liu, Tong ^{[1
]}

Luo, Liangshun ^{[1
]}

Wang, Liang ^{[1
]}

Guo, Nana ^{[1
]}

Li, Xinzhong ^{[1
]}

Chen, Ruirun ^{[1
]}

Su, Yanqing ^{[1
]}

Guo, Jingjie ^{[1
]}

Fu, Hengzhi ^{[1
]}

机构：

[1] Harbin Inst Technol, Sch Mat Sci & Engn, Natl Key Lab Precis Hot Proc Met, Harbin 150001, Peoples R China

来源：

MATERIALS & DESIGN | 2016年 / 97卷

基金：

中国国家自然科学基金;

关键词：

Microstructure evolution; TiAl alloy; Mushy zone; Thermal stabilization; Directional solidification; TIAL-SI ALLOYS; TEMPERATURE-GRADIENT; MECHANICAL-PROPERTIES; RESOLIDIFICATION; PHASE;

D O I：

10.1016/j.matdes.2016.02.098

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Thermal stabilization (TS) and directional solidification (DS) experiments were performed on Ti-43Al-3Si alloy in a Bridgman-type furnace. The effects of thermal stabilization time on the microstructure evolution of mushy zone and initial interface of directional solidification were investigated. The results show that the volume fraction of liquid in mushy zone and the length of mushy zone decrease as the thermal stabilization time increases. The concentrations of Al and Si exhibit a decreasing trend in the complete liquid zone with increasing TS time, while the solute concentrations of Al and Si in complete liquid zone are always higher than those of the original as-cast alloy. A long TS time promotes solute diffusion and provides a solute homogeneous initial interface for subsequent DS process. Isolated a grains and Ti5Si3 particles in mushy zone tend to coarsen with the increase of thermal stabilization time. Long time TS treatment also leads to growth of Ti5Si3 particles which may act as nucleation sites to terminate the continuous growth of dendrite and inheritance of the lamellar orientation. Directionally solidified samples with aligned lamellar structures can be obtained within 30 min TS treatment in Ti-43Al-3Si alloy. (C) 2016 Elsevier Ltd. All rights reserved.