A literature survey on the stability and significance of residual stresses during fatigue

被引:293
作者
McClung, R. C. [1 ]
机构
[1] SW Res Inst, San Antonio, TX 78228 USA
关键词
crack growth; cold expansion; fatigue; machining; peening; relaxation; residual stress; welding;
D O I
10.1111/j.1460-2695.2007.01102.x
中图分类号
TH [机械、仪表工业];
学科分类号
0802 ;
摘要
Many manufacturing processes can induce residual stresses in components. These residual stresses influence the mean stress during cyclic loading and so can influence the fatigue life. However, the initial residual stresses induced during manufacturing may not remain stable during the fatigue life. This paper provides a broad and extensive literature survey addressing the stability of surface and near-surface residual stress fields during fatigue, including redistribution and relaxation due to static mechanical load, repeated cyclic loads, thermal exposure and crack extension. The implications of the initial and evolving residual stress state for fatigue behaviour and life prediction are addressed, with special attention to fatigue crack growth. This survey is not a critical analysis; no detailed attempt is made to evaluate the relative merits of the different explanations and models proposed, to propose new explanations or models or to provide quantitative conclusions. Primary attention is given to the residual stresses resulting from four major classes of manufacturing operations: shot peening and related surface treatments, cold expansion of holes, welding and machining.
引用
收藏
页码:173 / 205
页数:33
相关论文
共 239 条
[1]  
ADAMS NJI, 1973, WELDING RES S, pS508
[2]   A new device for in situ residual stress measurement during fatigue testing [J].
Alam, AM ;
Chieragatti, R ;
Lavelle, B .
ECRS 5: PROCEEDINGS OF THE FIFTH EUROPEAN CONFERENCE ON RESIDUAL STRESSES, 2000, 347-3 :358-362
[3]   The effects of residual macrostresses and microstresses on fatigue crack propagation [J].
Almer, JD ;
Cohen, JB ;
Winholtz, RA .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1998, 29 (08) :2127-2136
[4]   The effects of residual macrostresses and microstresses on fatigue crack initiation [J].
Almer, JD ;
Cohen, JB ;
Moran, B .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2000, 284 (1-2) :268-279
[5]   Effects of mechanical surface treatment on fatigue failure in Ti-6Al-4V: Role of residual stresses and foreign-object damage [J].
Altenberger, I ;
Noster, U ;
Boyce, BL ;
Peters, JO ;
Scholtes, B ;
Ritchie, RO .
ECRS 6: PROCEEDINGS OF THE 6TH EUROPEAN CONFERENCE ON RESIDUAL STRESSES, 2002, 404-7 :457-462
[6]  
ALTENBERGER I, 2002, P 8 INT C SHOT PEEN, V8, P483
[7]  
[Anonymous], P 5 INT C TIT MUN FR
[8]  
[Anonymous], 2002, HDB RESIDUAL STRESS
[9]  
[Anonymous], 2003, MODERN MECH SURFACE
[10]  
[Anonymous], ASTM STP