Depolymerization of poly(L-lactic acid) under hydrothermal conditions

被引：15

作者：

Saeki, T ^{[1
]}

Tsukegi, T ^{[1
]}

Tsuji, H ^{[1
]}

Daimon, H ^{[1
]}

Fujie, K ^{[1
]}

机构：

[1] Toyohashi Univ Technol, Dept Ecol Engn, Toyohashi, Aichi 4418580, Japan

来源：

KOBUNSHI RONBUNSHU | 2004年 / 61卷 / 11期

关键词：

depolymerization; poly(L-lactic acid); enantiomer; hydrolysis; hydrothermal reaction;

D O I：

10.1295/koron.61.561

中图分类号：

O63 [高分子化学（高聚物）];

学科分类号：

070305 ; 080501 ; 081704 ;

摘要：

Poly(L-lactic acid) (PLLA) was readily depolymerized by hydrolysis under hydrothermal conditions in the absence of catalysts. The optimum condition for depolymerization of PLLA was found to be 220degreesC and 20 min. Under this condition, the recovery Of L-lactic acid was more than 95% without loss of optical purity. At a higher temperature (260-300degreesC), the optical purity decreased with increasing temperature, and a racemic mixture was formed at 300degreesC. Based on these results, the method was found to be promising for recycling PLLA by converting it to its monomer, L-lactic acid.

引用

页码：561 / 566

页数：6

共 50 条

[41] Nonisothermal crystallization of poly(L-lactic acid) promoted by polyols [J].

Yang, Biao ;

Wang, Huifang ;

Wan, Xinyu ;

Fan, Baomin ;

Sun, Hui .

POLYMERS FOR ADVANCED TECHNOLOGIES, 2023, 34 (07) :2189-2197

[42] Surface of gelatin modified poly(L-lactic acid) film [J].

Hou, X ;

Zhang, BL ;

She, F ;

Cui, YL ;

Shi, KY ;

Yao, KD .

CHINESE JOURNAL OF POLYMER SCIENCE, 2003, 21 (03) :277-283

[43] Blends of wheat straw modified with poly(L-lactic acid) [J].

Ding, Liang ;

Jiang, Li ;

Gao, Qin-Wei ;

Xu, Chen ;

Shangguan, Jia-Li .

Chemistry and Industry of Forest Products, 2015, 35 (03) :8-12

[44] Hydrolysis of poly(L-lactic acid) using microwave irradiation [J].

Hirao, Koichi ;

Shimamoto, Yoshie ;

Nakatsuchi, Yuta ;

Ohara, Hitomi .

POLYMER DEGRADATION AND STABILITY, 2010, 95 (01) :86-88

[45] Characterization and analyzation of the poly (L-lactic acid) (PLA) films [J].

Siriprom, W. ;

Sangwaranatee, N. ;

Herman ;

Chantarasunthon, K. ;

Teanchai, K. ;

Chamchoi, N. .

MATERIALS TODAY-PROCEEDINGS, 2018, 5 (07) :14803-14806

[46] PREPARATION AND MISCRIBILITY STUDIES OF POLY(L-LACTIC ACID)/POLY(ASPARTIC ACID-co-LACTIC ACID)BLENDS [J].

Yao Junyan ;

Yang Qingfang ;

Shu Xiaojun ;

Zhang Aijun ;

Du Jianghua .

ACTA POLYMERICA SINICA, 2008, (10) :929-934

[47] SURFACE OF GELATIN MODIFIED POLY(L-LACTIC ACID)FILM [J].

姚康德 .

Chinese Journal of Polymer Science, 2003, (03) :277-283

[48] Influence of α′-/α-crystal polymorphism on properties of poly(l-lactic acid) [J].

Di Lorenzo, Maria Laura ;

Androsch, Rene .

POLYMER INTERNATIONAL, 2019, 68 (03) :320-334

[49] Isothermal melt crystallization kinetics of poly(L-lactic acid) [J].

Urbanovici, E ;

Schneider, HA ;

Brizzolara, D ;

Cantow, HJ .

JOURNAL OF THERMAL ANALYSIS, 1996, 47 (04) :931-939

[50] Crystalline morphology of poly(L-lactic acid) thin films [J].

Li, Haidong ;

Nie, Wei ;

Deng, Chao ;

Chen, Xuesi ;

Ji, Xiangling .

EUROPEAN POLYMER JOURNAL, 2009, 45 (01) :123-130

← 1 2 3 4 5 →