Effects of Activator Properties and Ferrochrome Slag Aggregates on the Properties of alkali-activated Blast Furnace Slag Mortars

被引:22
作者
Elibol, Caner [1 ]
Sengul, Ozkan [1 ]
机构
[1] Istanbul Tech Univ, Fac Civil Engn, TR-80626 Istanbul, Turkey
关键词
Blast furnace slag; Alkali activation; Activator; Ferrochrome slag aggregate; Compressive strength; Electrical resistivity; ELECTRICAL-RESISTIVITY MEASUREMENTS; MECHANICAL-PROPERTIES; COMPRESSIVE STRENGTH; DRYING SHRINKAGE; CONCRETE; DURABILITY; PRODUCTS; CHLORIDE; CEMENTS;
D O I
10.1007/s13369-015-1910-8
中图分类号
O [数理科学和化学]; P [天文学、地球科学]; Q [生物科学]; N [自然科学总论];
学科分类号
07 ; 0710 ; 09 ;
摘要
An innovative way of utilizing ground granulated blast furnace slag is to activate it using alkaline materials. The main objective of this study was to investigate the effects of activator type and curing conditions on the compressive strength and electrical resistivity of alkali-activated ground granulated blast furnace slag mortars. To obtain mortars consisting of waste materials was also an objective of the study. Ferrochrome slag was used as aggregate in some mixtures to investigate the effect of this waste material when used as an aggregate. As a result, both the binder and the aggregates were waste materials in some of the mixtures prepared. Test results indicated that for the standard water curing at 20 degrees C, the compressive strength of the alkali-activated mortars was lower compared to that of the Portland cement, although these strengths may be considered enough for low and moderate strength applications. Higher strengths were obtained with the use of hot water curing. The test results demonstrated that the alkali-activated blast furnace slag containing waste ferrochrome slag as aggregate may achieve strength properties comparable or even higher than the ones produced with ordinary Portland cement and natural aggregates. Electrical resistivities of these alkali-activated mixtures were also significantly higher compared to that of the reference mixture.
引用
收藏
页码:1561 / 1571
页数:11
相关论文
共 54 条
[1]   Alkali activation of a slag at ambient and elevated temperatures [J].
Altan, Ekin ;
Erdogan, Sinan T. .
CEMENT & CONCRETE COMPOSITES, 2012, 34 (02) :131-139
[2]  
[Anonymous], 2013, 12620 EN
[3]  
[Anonymous], 2005, EN 196-1.
[4]  
[Anonymous], 2006, ASTM C989
[5]   Influence of activator on the strength and drying shrinkage of alkali-activated slag mortar [J].
Atis, Cengiz Duran ;
Bilim, Cahit ;
Celik, Oezlem ;
Karahan, Okan .
CONSTRUCTION AND BUILDING MATERIALS, 2009, 23 (01) :548-555
[6]   Effect of activator type and content on properties of alkali-activated slag mortars [J].
Aydin, Serdar ;
Baradan, Bulent .
COMPOSITES PART B-ENGINEERING, 2014, 57 :166-172
[7]   Effect of elevated temperature curing on properties of alkali-activated slag concrete [J].
Bakharev, T ;
Sanjayan, JG ;
Cheng, YB .
CEMENT AND CONCRETE RESEARCH, 1999, 29 (10) :1619-1625
[8]   Influence of activator type on hydration kinetics, hydrate assemblage and microstructural development of alkali activated blast-furnace slags [J].
Ben Haha, M. ;
Le Saout, G. ;
Winnefeld, F. ;
Lothenbach, B. .
CEMENT AND CONCRETE RESEARCH, 2011, 41 (03) :301-310
[9]  
Bhat G., 2019, BS EN 1015-3 Methods of Test for Mortar Masonry-Part 3: Determination of Consistence of Fresh Mortar (By Flow Table), Patent No. [EPL3779, 3779]
[10]  
Bijen J.G., 1996, Blast Furnace Slag Cement