Tribological behaviour of oxide/graphite composite coatings deposited using electrolytic plasma process

被引：27

作者：

Nie, X ^{[1
]}

Wang, L ^{[1
]}

Konca, E ^{[1
]}

Alpas, AT ^{[1
]}

机构：

[1] Univ Windsor, Dept Mech Automot & Mat Engn, Windsor, ON N9B 3P4, Canada

来源：

SURFACE & COATINGS TECHNOLOGY | 2004年 / 188卷

基金：

加拿大自然科学与工程研究理事会; 加拿大创新基金会;

关键词：

aluminium alloy; wear resistance; friction coating; oxide/lubricant composite coatings;

D O I：

10.1016/j.surfcoat.2004.08.025

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The research was intended to deposit a low-friction coating on a cast Al-Si alloy substrate using an electrolytic plasma process (EPP) and then investigate tribological behaviour of the coating. The coating was designed to have a bi-layered structure consisting of an oxide underlayer and oxide/graphite lubricant composite top layer. A symmetrical AC power supply, operating at a relatively low voltage (less than 250 V), was used in the EPP treatment. Tribological properties of coatings with different thicknesses were tested using a pin-on-disc tribometer. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used to characterize microstructures and morphologies of the coatings. It was found that an AC power could be successfully used to produce oxide and oxide/graphite composite coatings on aluminium alloys. Both thick (50 gm) oxide and oxide/graphite composite coatings had high wear. However, the oxide/graphite composite coating was superior to the single-layered oxide coating because it had a low coefficient of friction (0.22) and exhibited good compatibility with the steel counterface during dry tribological testing. (C) 2004 Elsevier B.V. All rights reserved.

引用

页码：207 / 213

页数：7

共 15 条

[1]

[Anonymous], 1991, ADV SURFACE COATINGS

[2]

CSOKAN P, 1962, ELECTROPLAT MET FINI, V5, P75

[3]

KAPE JM, 1957, MET IND, V91, P63

[4] Abrasive wear/corrosion properties and TEM analysis of Al2O3 coatings fabricated using plasma electrolysis [J].

Nie, X ;

Meletis, EI ;

Jiang, JC ;

Leyland, A ;

Yerokhin, AL ;

Matthews, A .

SURFACE & COATINGS TECHNOLOGY, 2002, 149 (2-3) :245-251

[5] Deposition of layered bioceramic hydroxyapatite/TiO2 coatings on titanium alloys using a hybrid technique of micro-arc oxidation and electrophoresis [J].

Nie, X ;

Leyland, A ;

Matthews, A .

SURFACE & COATINGS TECHNOLOGY, 2000, 125 (1-3) :407-414

[6] Deposition of duplex Al2O3/DLC coatings on Al alloys for tribological applications using a combined micro-arc oxidation and plasma-immersion ion implantation technique [J].

Nie, X ;

Wilson, A ;

Leyland, A ;

Matthews, A .

SURFACE & COATINGS TECHNOLOGY, 2000, 131 (1-3) :506-513

[7]

SHASHKOV P, 2004, P INT C MET COAT THI, P53

[8] Mechanisms underlying the formation of thick alumina coatings through the MAO coating technology [J].

Sundararajan, G ;

Krishna, LR .

SURFACE & COATINGS TECHNOLOGY, 2003, 167 (2-3) :269-277

[9] Characterization of wear protective Al-Si-O coatings formed on Al-based alloys by micro-arc discharge treatment [J].

Voevodin, AA ;

Yerokhin, AL ;

Lyubimov, VV ;

Donley, MS ;

Zabinski, JS .

SURFACE & COATINGS TECHNOLOGY, 1996, 86-7 (1-3) :516-521

[10] Scuffing and wear behavior of aluminum piston skirt coatings against aluminum cylinder bore [J].

Wang, YC ;

Tung, SC .

WEAR, 1999, 225 :1100-1108

← 1 2 →