Thermo-mechanical analysis of strength degradation of 30SiMn2MoVA gun barrel material during continuous shooting

被引：16

作者：

Chen, Junyu ^{[1
]}

Wang, Weijie ^{[2
]}

Jin, Pengfei ^{[1
]}

Dou, Caihong ^{[1
]}

Zhao, Chao ^{[1
]}

Li, Qiang ^{[2
]}

Zhang, Cheng ^{[1
]}

机构：

[1] Univ Sci & Technol Beijing, State Key Lab Adv Met & Mat, Beijing, Peoples R China

[2] North Univ China, Coll Mechatron Engn, Taiyuan, Peoples R China

来源：

ENGINEERING FAILURE ANALYSIS | 2022年 / 139卷

关键词：

30SiMn2MoVA steel; High temperature softening; Failure mechanism; Gun barrel; HEAT-TRANSFER; EROSION;

D O I：

10.1016/j.engfailanal.2022.106438

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

The internal bore of a machine gun barrel is subjected to the complex effects of cyclic hightemperature and mechanical loadings during the continuous shooting process, resulting in the accumulation of bore damages and eventually the end of the lifespan. The correlation between the ballistic performances and the material properties is a critical issue for the development of gun barrels with a long lifespan. However, it is still not fully understood yet. In this study, the thermomechanical analysis of the strength degradation of 30SiMn2MoVA gun barrel steel during continuous shooting is investigated. Irregular rifling deformation of the failed machine gun barrel with a 12.7 mm caliber was observed. Mechanical tensile tests revealed that severe softening occurs in the 30SiMn2MoVA steel when the temperature exceeded 600 degrees C, where the yield strength decreased significantly from 862 MPa at room temperature to 114 MPa at 700 degrees C. Transmission electron microscope observations further revealed that the recrystallization of martensitic lath and the growth of cementite softened the gun barrel steel. Moreover, the finite element models are established using the Abaqus software for the evolution of the temperature and stress of the internal wall within 180 cycles. This shows that the peak temperature increases to 730-740 degrees C and the peak total stress exceeds 246 MPa during 170-180 cycles, which is much higher than the yield strength of 30SiMn2MoVA gun barrel steel. Therefore, the strength of gun barrel steel at 700 degrees C can be suggested as the key parameter for the development of long-life gun barrels for continuous shooting.

引用

页数：11

共 31 条

[1]

Ablyaz T.R., 2016, SURF REV LETT, V24, P27

[2] UNSTEADY INTERNAL BOUNDARY-LAYER ANALYSIS APPLIED TO GUN BARREL WALL HEAT-TRANSFER [J].

ADAMS, MJ ;

KRIER, H .

INTERNATIONAL JOURNAL OF HEAT AND MASS TRANSFER, 1981, 24 (12) :1925-1935

[3]

Ahmad I, 2020, WEAR, V5, P444

[4]

Akçay M, 2014, ISI BILIM TEK DERG, V34, P75

[5]

Corner J., 1950, J CRIMINAL LAW CRIMI

[6]

Courtney M, 2007, PHYSICS, V17, P15

[7] A thermochemical approach for the determination of convection heat transfer coefficients in a gun barrel [J].

Degirmenci, Ercan ;

Dirikolu, M. Husnu .

APPLIED THERMAL ENGINEERING, 2012, 37 :275-279

[8]

Dong X., 2020, APPL THERM ENG, V185, P116

[9]

Grethlein C.E., 2004, AMPTIAC Q, V8, P49

[10] Design of Gun Barrel Exterior Wall Temperature Measurement Device [J].

Jia, Changzhi ;

Xu, Dongsheng ;

Liu, Guangsheng ;

He, Yaoxin .

FRONTIERS OF MECHANICAL ENGINEERING AND MATERIALS ENGINEERING, PTS 1 AND 2, 2012, 184-185 :1546-1549

← 1 2 3 4 →