Investigations on the microstructure and room temperature fracture toughness of directionally solidified NiAl-Cr(Mo) eutectic alloy

被引：45
作者：
Shang, Zhao [1 ]
Shen, Jun [1 ]
Wang, Lei [1 ]
Du, Yujun [1 ]
Xiong, Yilong [1 ]
Fu, Hengzhi [1 ]
机构：
[1] Northwestern Polytech Univ, State Key Lab Solidificat Proc, Xian 710072, Peoples R China
来源：
INTERMETALLICS | 2015年 / 57卷
基金：
中国国家自然科学基金;
关键词：
Nickel aluminides; based on NiAl; Crack propagation; Fracture toughness; Crystal growth; Microstructure; Aero-engine components; MECHANICAL-PROPERTIES; NIAL-MO; COMPRESSIVE PROPERTIES; GROWTH; CR; DEFORMATION; TRANSITION; STRENGTH;
D O I：
10.1016/j.intermet.2014.09.012
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
The microstructures and room temperature fracture toughness of directionally solidified NiAl-xCr-6Mo (x = 28, 32 and 36 at%) alloys were investigated. Fully eutectic microstructure could be obtained in the alloys over a wide composition range. High temperature gradient could increase the planar/cellular transition rate and expand the eutectic coupled growth zone. The volume fraction of Cr(Mo) strengthening phase increased with the increasing content of Cr, accordingly, the fracture toughness of NiAl -Cr(Mo) alloys also gradually increased. The fracture toughness of 26.15 MPa m(1/2) was obtained in the NiAl-36Cr-6Mo hypereutectic alloy solidified at withdrawal rate of 10 mu m/s and temperature gradient of 600 K/cm, which is the highest value in the NiAl Cr Mo alloy system until now. Well-aligned microstructure was beneficial to the enhancement of the fracture toughness, while the existence of primary phase seriously deteriorated the toughness. All the directionally solidified NiAl Cr(Mo) alloy failed as brittle quasi-cleavage fracture. Some toughening mechanisms, such as crack bridging, crack nucleation, crack blunting, crack deflection, interface debonding and shear ligament toughening as well as linkage of microcracks were observed. In addition, mobile dislocation generated from the interface also had significant influence on the toughness. (C) 2014 Elsevier Ltd. All rights reserved.
引用
收藏
页码：25 / 33
页数：9
相关论文
共 45 条
[11]   Elastic properties of B2-ordered NiAl and NiAl-X (Cr, Mo, W) alloys [J].
Frommeyer, G. ;
Rablbauer, R. ;
Schaefer, H. J. .
INTERMETALLICS, 2010, 18 (03) :299-305
[12]   BRITTLE-FRACTURE AND GRAIN-BOUNDARY CHEMISTRY OF MICROALLOYED NIAL [J].
GEORGE, EP ;
LIU, CT .
JOURNAL OF MATERIALS RESEARCH, 1990, 5 (04) :754-762
[13]   Effect of Ho on the microstructure and compressive properties of NiAl-based eutectic alloy [J].
Guo, J. T. ;
Sheng, L. Y. ;
Tian, Y. X. ;
Zhou, L. Z. ;
Ye, H. Q. .
MATERIALS LETTERS, 2008, 62 (23) :3910-3912
[14]   THE MECHANICS OF CRACK-GROWTH IN LAYERED MATERIALS [J].
HE, MY ;
HEREDIA, FE ;
WISSUCHEK, DJ ;
SHAW, MC ;
EVANS, AG .
ACTA METALLURGICA ET MATERIALIA, 1993, 41 (04) :1223-1228
[15]   THE FRACTURE-RESISTANCE OF DIRECTIONALLY SOLIDIFIED DUAL-PHASE NIAL REINFORCED WITH REFRACTORY-METALS [J].
HEREDIA, FE ;
HE, MY ;
LUCAS, GE ;
EVANS, AG ;
DEVE, HE ;
KONITZER, D .
ACTA METALLURGICA ET MATERIALIA, 1993, 41 (02) :505-511
[16]  
HUNT JD, 1967, T METALL SOC AIME, V239, P864
[17]   PROCESSING AND MECHANICAL-PROPERTIES OF IN-SITU COMPOSITES FROM THE NIAL-CR AND THE NIAL-(CR,MO) EUTECTIC SYSTEMS [J].
JOHNSON, DR ;
CHEN, XF ;
OLIVER, BF ;
NOEBE, RD ;
WHITTENBERGER, JD .
INTERMETALLICS, 1995, 3 (02) :99-113
[18]   DIRECTIONAL SOLIDIFICATION AND MECHANICAL-PROPERTIES OF NIAL-NIALTA ALLOYS [J].
JOHNSON, DR ;
CHEN, XF ;
OLIVER, BF ;
NOEBE, RD ;
WHITTENBERGER, JD .
INTERMETALLICS, 1995, 3 (02) :141-152
[19]   FRACTURE-BEHAVIOR OF DIRECTIONALLY SOLIDIFIED NIAL-MO AND NIAL-V EUTECTICS [J].
JOSLIN, SM ;
CHEN, XF ;
OLIVER, BF ;
NOEBE, RD .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1995, 196 (1-2) :9-18
[20]   FRACTURE-TOUGHNESS OF NIAL AND NIAL-BASED COMPOSITES [J].
KUMAR, KS ;
MANNAN, SK ;
VISWANADHAM, RK .
ACTA METALLURGICA ET MATERIALIA, 1992, 40 (06) :1201-1222
12345