Corrosion of carbon steel C1010 in the presence of iron oxidizing bacteria Acidithiobacillus ferrooxidans

被引：90

作者：

Wang, Hua ^{[1
]}

Ju, Lu-Kwang ^{[1
]}

Castaneda, Homero ^{[1
]}

Cheng, Gang ^{[1
]}

Newby, Bi-min Zhang ^{[1
]}

机构：

[1] Univ Akron, Dept Chem & Biomol Engn, Akron, OH 44325 USA

来源：

CORROSION SCIENCE | 2014年 / 89卷

关键词：

Carbon steel; Weight loss; Acid corrosion; Microbiological corrosion; Pitting Corrosion; MICROBIOLOGICALLY INFLUENCED CORROSION; STAINLESS-STEEL; FERROBACILLUS-FERROOXIDANS; BEHAVIOR; SULFATE; 304-STAINLESS-STEEL; ENVIRONMENTS; THIOBACILLUS; OXIDATION; PIPELINE;

D O I：

10.1016/j.corsci.2014.09.005

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In this study, corrosion behaviors of carbon steel C1010 in the presence of an acidophilic, iron-oxidizing bacterial species Acidithiobacillus ferrooxidans were examined. Results showed that A. ferrooxidans cells, with or without attaching to C1010 steel, accelerated its corrosion at a rate of 3-6x those of acidic water, at a pH of 2, without cells. A. ferrooxidans oxidized Fe2+ to Fe3+ as an energy source and the produced Fe3+ rapidly oxidized Fe-0 to Fe2+ was proposed and verified as the reason. In addition, severe pitting corrosion was found on the C1010 steel surface in solutions containing A. ferrooxidans cells. (C) 2014 Elsevier Ltd. All rights reserved.

引用

页码：250 / 257

页数：8

共 50 条

[1] Corrosion Behavior of Cast Iron in the Presence of Acidithiobacillus Ferrooxidans
Lin, Li
Liu, Cheng
Fu, Lei
Zeng, Ying
Gong, Min
Cui, Xue Jun
Meng, Junchen
Huang, Xin Jie
INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2021, 16 (02): : 1 - 17
[2] Corrosion behavior of carbon steel in the presence of sulfate reducing bacteria and iron oxidizing bacteria cultured in oilfield produced water
Liu, Hongwei
Fu, Chaoyang
Gu, Tingyue
Zhang, Guoan
Lv, Yalin
Wang, Haitao
Liu, Hongfang
CORROSION SCIENCE, 2015, 100 : 484 - 495
[3] Corrosion of steel due to iron oxidizing bacteria
Sachan, Reena
Singh, Ajay Kumar
ANTI-CORROSION METHODS AND MATERIALS, 2019, 66 (01) : 19 - 26
[4] The effect of magneticfield on biomineralization and corrosion behavior of carbon steel induced by iron-oxidizing bacteria
Liu, Hongwei
Gu, Tingyue
Zhang, Guoan
Cheng, Yufeng
Wang, Haitao
Liu, Hongfang
CORROSION SCIENCE, 2016, 102 : 93 - 102
[5] Corrosion inhibition of carbon steel in CO2-containing oilfield produced water in the presence of iron-oxidizing bacteria and inhibitors
Liu, Hongwei
Gu, Tingyue
Zhang, Guoan
Wang, Wei
Dong, Shuang
Cheng, Yufeng
Liu, Hongfang
CORROSION SCIENCE, 2016, 105 : 149 - 160
[6] Study of inhibition effect of pyridinium salt derivative on corrosion of C1010 carbon steel in saline solution
Shihab, Mehdi Salih
Nazari, Mehdi Honarvar
Fay, Laura
PROTECTION OF METALS AND PHYSICAL CHEMISTRY OF SURFACES, 2016, 52 (04) : 714 - 720
[7] Corrosion behavior of carbon steel in the presence of two novel iron-oxidizing bacteria isolated from sewage treatment plants
Ashassi-Sorkhabi, H.
Moradi-Haghighi, M.
Zarrini, G.
Javaherdashti, R.
BIODEGRADATION, 2012, 23 (01) : 69 - 79
[8] Electrochemical corrosion behavior and mechanism of iron-oxidizing bacteria Thiobacillus ferrooxidans from acid mine drainage on Q235 carbon steel
Lin, Li
Tsou, Chi-Hui
Dou, Baojie
Yan, Shisen
Zeng, Ying
Gong, Min
NEW JOURNAL OF CHEMISTRY, 2022, 46 (42) : 20279 - 20291
[9] Engineering the iron-oxidizing chemolithoautotroph Acidithiobacillus ferrooxidans for biochemical production
Kernan, Timothy
Majumdar, Sudipta
Li, Xiaozheng
Guan, Jingyang
West, Alan C.
Banta, Scott
BIOTECHNOLOGY AND BIOENGINEERING, 2016, 113 (01) : 189 - 197
[10] The corrosion behavior and mechanism of carbon steel induced by extracellular polymeric substances of iron-oxidizing bacteria
Liu, Hongwei
Gu, Tingyue
Asif, Muhammad
Zhang, Guoan
Liu, Hongfang
CORROSION SCIENCE, 2017, 114 : 102 - 111

← 1 2 3 4 5 →