Fabrication of ultrafine Nd-Fe-B powder by a modified reduction-diffusion process

被引：8
|
作者：
Jang, T. S.
Lee, D. H.
Yu, J. H.
Choi, C. J.
Seo, W. S.
Lee, Y. H.
机构：
[1] Department of Electronic Materials Engineering, Sunmoon University
[2] Powder Materials Research Center, Korea Institute of Machinery and Materials
[3] Advanced Materials Analysis and Evaluation Center, Korea Institute of Ceramic Engineering and Technology
来源：
RARE METALS | 2006年 / 25卷 / 223-226期
关键词：
NdFeB powder; spray drying; reduction-diffusion process; Nd2Fe14B; magnetic powder;
D O I：
10.1016/S1001-0521(08)60086-8
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In order to obtain ultrafine Nd-Fe-B powder, a spray-dried precursor was treated by reduction-diffusion (R/D) process. And, unlike the conventional R/D process, calcium reduction that is a crucial step for the formation of Nd2Fe14B was performed without conglomerating the precursor with Ca powder. By adopting this modified process, it is possible to synthesize the hard magnetic Nd2Fe14B at the reaction temperature as low as 850 degrees C. The average size of Nd2Fe14B particles that are uniformly distributed in the optimally treated powder was << 1 mu m. Most Nd2Fe14B particles were enclosed with thin layers of Nd-rich phase. Typical magnetic properties of such powder without eliminating impurity CaO were H-i(c) = similar to 5.9 kOe, B-r = similar to 5.5 kG, and (BH)(max) = similar to 6 MGOe.
引用
收藏
页码：223 / 226
页数：4
相关论文
共 50 条
  • [31] Explosive compaction of Nd-Fe-B powder
    Ando, S
    Mine, Y
    Takashima, K
    Itoh, S
    Tonda, H
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 1999, 85 (1-3) : 142 - 147
  • [32] Powder consolidation of Nd-Fe-B/α-Fe nanocomposite materials by cold deformation process
    Hosokawa, Akihide
    Takagi, Kenta
    AIP ADVANCES, 2018, 8 (09):
  • [33] Enhanced Nd-Rich Phase and Oxygen Control in Reduction-Diffusion Powders via Tailored Washing Process for Additive-Free Sintering of Fine Nd-Fe-B Particles
    Galkin, Vitalii
    Kuchi, Rambabu
    Kwon, Soon-Jae
    Kim, Tae-hoon
    Lee, Jung-goo
    Jeong, Jong-Ryul
    Kim, Dongsoo
    JOURNAL OF MAGNETICS, 2024, 29 (01) : 1 - 9
  • [34] Feasibility of Nd Substitution in (La, Nd)(Fe, Si)13 Magnetocaloric Compound Obtained by the Reduction-Diffusion Process
    Eggert, B. G. F.
    Teixeira, C. S.
    Lopes, L. U.
    Wendhausen, P. A. P.
    IEEE TRANSACTIONS ON MAGNETICS, 2016, 52 (05)
  • [35] Fabrication of low-cost Nd-Fe-B sintered magnets reusing ultrafine powders
    Cui, X. G.
    Yan, M.
    Ma, T. Y.
    Luo, W.
    Tu, S. J.
    MATERIALS SCIENCE AND TECHNOLOGY, 2010, 26 (02) : 193 - 196
  • [36] THE SYNTHESIS OF ND-FE-CO-B BY REDUCTION-DIFFUSION AND ITS MAGNETIC-PROPERTIES
    SUN, GF
    CHEN, JF
    DAHL, W
    KLAAR, HJ
    BURCHARD, WG
    JOURNAL OF APPLIED PHYSICS, 1988, 64 (10) : 5519 - 5521
  • [37] Study on fabrication process of anisotropic injection bonded Nd-Fe-B magnets
    Zhang Xiao-lei
    Zhu Ming-yuan
    Li Ying
    Yang Qiu-ping
    Jin Hong-ming
    Jiang Juan
    Tian Ye
    Luo Yang
    JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2006, 13 : 286 - 288
  • [38] INFLUENCE OF WASHING PROCESS ON THE PROPERTIES OF NANOCRYSTALLINE Nd-Fe-B MAGNET POWDER PREPARED BY MODIFIED R-D PROCESS
    Jang, T. S.
    Lee, D. H.
    Namkung, S.
    REVIEWS ON ADVANCED MATERIALS SCIENCE, 2011, 28 (02) : 212 - 216
  • [39] Properties of Nd-Fe-B powder explosively compacted
    Eskandari, H.
    Gholamipouri, R.
    EXPLOSION, SHOCK WAVE AND HIGH-ENERGY REACTION PHENOMENA, 2011, 673 : 237 - +
  • [40] Recent progress of grain boundary diffusion process of Nd-Fe-B magnets
    Chen, Fugang
    JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2020, 514
12345