Studies on some alkali-phosphate glasses containing antimony and iron oxides

被引：8
作者：
Mostafa, AG
Yahya, GA [1 ]
Ali, KA
Gabr, M
Gomma, NS
Eissa, NA
机构：
[1] Al Azhar Univ, Fac Sci, Dept Phys, Nasr City, Cairo, Egypt
[2] S Valley Univ, Fac Sci Aswan, Dept Phys, Aswan 81528, Egypt
[3] Zagazig Univ, Fac Sci, Dept Phys, Zagazig, Egypt
[4] Al Azhar Univ, Fac Sci, Dept Phys, Women Branch, Nasr City, Cairo, Egypt
来源：
SOLID STATE COMMUNICATIONS | 2004年 / 131卷 / 11期
关键词：
phosphate glasses; glass structure; antimony and iron dopants impurities; Mossbauer spectroscopy;
D O I：
10.1016/j.ssc.2004.03.029
中图分类号：
O469 [凝聚态物理学];
学科分类号：
070205 ;
摘要：
The effect of heat treatment on the Fe2+/Fe3+ ratio in some alkali phosphate glasses containing antimony and iron oxides has been investigated. Differential thermal analysis, Mossbauer spectroscopy, magnetic susceptibility and density measurements as well as the molar volume calculations were used in this study. The obtained data indicate that all glasses show approximately unchangeable stability. It is found, from the area under the Mossbauer absorption spectra that ferrous transformed gradually to ferric ions and the transformation rate constant was found to be 48 min(-1). The elapsed time was found to be 160 min. This transformation represents a first-order solid state reaction. The molar magnetic susceptibility measurements confirm the above results. (C) 2004 Elsevier Ltd. All rights reserved.
引用
收藏
页码：729 / 734
页数：6
相关论文
共 21 条
[1]  
[Anonymous], 1982, CHEM GLASSES
[2]  
AVERY HE, 1977, BASIC REACTION KINET
[3]   MOSSBAUER SPECTROSCOPIC INVESTIGATION OF SOME IRON-CONTAINING SODIUM-PHOSPHATE GLASSES [J].
CONCAS, G ;
CONGIU, F ;
MANCA, E ;
MUNTONI, C ;
PINNA, G .
JOURNAL OF NON-CRYSTALLINE SOLIDS, 1995, 193 :175-178
[4]  
Cotton F. A., 1972, ADV INORG CHEM, P1145
[5]  
DOWIDAR H, 1998, J NONCRYST SOLIDS, V24, P539
[6]   Conductivity and dielectric behaviour of iron sodium phosphate glasses [J].
El-Desoky, MM ;
Tahoon, K ;
Hassaan, MY .
MATERIALS CHEMISTRY AND PHYSICS, 2001, 69 (1-3) :180-185
[7]  
El-Eskandarany MS, 2001, J ALLOY COMPD, V314, P286, DOI 10.1016/S0925-8388(00)01245-7
[8]  
ELHADI ZA, 1993, GLASS CERAM B, V40, P104
[9]  
Hassaan MY, 2001, J RADIOANAL NUCL CH, V249, P595
[10]  
KASHIF I, 1988, PHYS CHEM GLASSES, V29, P72
123