Stress corrosion cracking in the heat affected zone of a stainless steel 308L-316L weld joint in primary water

被引：70
作者：
Dong, Lijin [1 ,2 ]
Peng, Qunjia [1 ]
Han, En-Hou [1 ]
Ke, Wei [1 ]
Wang, Lei [2 ]
机构：
[1] Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China
[2] Northeastern Univ, Key Lab Anisotropy & Texture Mat, Minist Educ, Shenyang 110819, Peoples R China
来源：
CORROSION SCIENCE | 2016年 / 107卷
基金：
中国国家自然科学基金;
关键词：
Stainless steel; SEM; TEM; Stress corrosion; Welding; HIGH-TEMPERATURE WATER; PWR PRIMARY WATER; LOW-ALLOY STEEL; GROWTH; MICROSTRUCTURE; ENVIRONMENT; CHEMISTRY; REGION; 690TT;
D O I：
10.1016/j.corsci.2016.02.030
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Stress corrosion cracking (SCC) in the heat affected zone (HAZ) of a stainless steel 308L-316L weld joint in primary water of pressurized water reactor was investigated. Stress corrosion crack growth in the HAZ was observed in off-normal primary water chemistry with dissolved oxygen, but not in normal primary water chemistry with dissolved hydrogen. This suggests that it is unlikely a stress corrosion crack propagating in the HAZ could reach the fusion boundary and penetrate into the weld metal under normal primary water chemistry conditions. Microstructure analysis of the crack tip suggests that the SCC follows the slip-oxidation mechanism. (C) 2016 Elsevier Ltd. All rights reserved.
引用
收藏
页码：172 / 181
页数：10
相关论文
共 50 条
[41]   Stress corrosion cracking behavior of AISI 316L stainless steel treated by surface mechanical grinding [J].
Yang, Chongwen ;
Ye, Yuanyuan ;
Zhang, Wenqian ;
Wang, Xuelin .
ENGINEERING FRACTURE MECHANICS, 2023, 292
[42]   Effects of Cryogenic Milling on Stress Corrosion Cracking Resistance of AISI 316L Austenitic Stainless Steel [J].
Yang, Chongwen ;
Zhang, Wenqian ;
Hu, Yujin ;
Wang, Xuelin .
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2020, 29 (11) :7104-7114
[43]   Effect of pH on corrosion behavior of 316L stainless steel in hydrogenated high temperature water [J].
Wang, Jiazhen ;
Wang, Jianqiu ;
Ming, Hongliang ;
Zhang, Zhiming ;
Han, En-Hou .
MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2018, 69 (05) :580-589
[44]   Effects of Corrosion Potential, Dissolved Oxygen, and Chloride on the Stress Corrosion Cracking Susceptibility of a 316NG Stainless Steel Weld Joint [J].
Wang, Jiamei ;
Su, Haozhan ;
Ajmand, Farzin ;
Zhang, Lefu ;
Chen, Kai .
CORROSION, 2019, 75 (08) :946-959
[45]   Deflection behaviour of corrosion crack growth in the heat affected zone of CrNiMoV steel welded joint [J].
Luo, Linghua ;
Huang, Yuhui ;
Xuan, Fu-Zhen .
CORROSION SCIENCE, 2017, 121 :11-21
[46]   Effect of post-irradiation annealing on microstructure and corrosion of proton-irradiated 308L stainless steel weld metal [J].
Lin, Xiaodong ;
Han, En-Hou ;
Peng, Qunjia ;
Ke, Wei ;
Jiao, Zhijie .
CORROSION SCIENCE, 2020, 175
[47]   Intergranular oxidation of 316L stainless steel in the PWR primary water environment [J].
Matthews, R. P. ;
Knusten, R. D. ;
Westraadt, J. E. ;
Couvant, T. .
CORROSION SCIENCE, 2017, 125 :175-183
[48]   Stress corrosion cracking of cold worked 316L stainless steel in high temperature and high pressure pure water [J].
Du, Dong-Hai ;
Shen, Zhao ;
Chen, Kai ;
Yu, Lun ;
Zhang, Le-Fu ;
Shi, Xiu-Qiang ;
Xu, Xue-Lian .
Gongcheng Kexue Xuebao/Chinese Journal of Engineering, 2015, 37 (02) :196-203
[49]   Improving the Intergranular Corrosion Resistance of Aged 316L Stainless Steel Heat Affected Zone by Electropulsing Beneath the Critical Temperature [J].
Ding, Shengli ;
Yan, Longge ;
Cheng, Xuehao ;
Zhang, Xinfang .
JOM, 2021, 73 (12) :3928-3940
[50]   Effects of surface finishes, heat treatments and printing orientations on stress corrosion cracking behavior of laser powder bed fusion 316L stainless steel in high-temperature water [J].
Que, Zaiqing ;
Riipinen, Tuomas ;
Ferreiros, Pedro ;
Goel, Sneha ;
Sipila, Konsta ;
Saario, Timo ;
Ikalainen, Tiina ;
Toivonen, Aki ;
Revuelta, Alejandro .
CORROSION SCIENCE, 2024, 233
12345