Stress corrosion cracking in the heat affected zone of a stainless steel 308L-316L weld joint in primary water

被引：70

作者：

Dong, Lijin ^{[1
,2
]}

Peng, Qunjia ^{[1
]}

Han, En-Hou ^{[1
]}

Ke, Wei ^{[1
]}

Wang, Lei ^{[2
]}

机构：

[1] Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China

[2] Northeastern Univ, Key Lab Anisotropy & Texture Mat, Minist Educ, Shenyang 110819, Peoples R China

来源：

CORROSION SCIENCE | 2016年 / 107卷

基金：

中国国家自然科学基金;

关键词：

Stainless steel; SEM; TEM; Stress corrosion; Welding; HIGH-TEMPERATURE WATER; PWR PRIMARY WATER; LOW-ALLOY STEEL; GROWTH; MICROSTRUCTURE; ENVIRONMENT; CHEMISTRY; REGION; 690TT;

D O I：

10.1016/j.corsci.2016.02.030

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Stress corrosion cracking (SCC) in the heat affected zone (HAZ) of a stainless steel 308L-316L weld joint in primary water of pressurized water reactor was investigated. Stress corrosion crack growth in the HAZ was observed in off-normal primary water chemistry with dissolved oxygen, but not in normal primary water chemistry with dissolved hydrogen. This suggests that it is unlikely a stress corrosion crack propagating in the HAZ could reach the fusion boundary and penetrate into the weld metal under normal primary water chemistry conditions. Microstructure analysis of the crack tip suggests that the SCC follows the slip-oxidation mechanism. (C) 2016 Elsevier Ltd. All rights reserved.

引用

页码：172 / 181

页数：10

共 49 条

[21] Effects of cold working degrees on grain boundary characters and strain concentration at grain boundaries in Alloy 600 [J].

Hou, J. ;

Peng, Q. J. ;

Lu, Z. P. ;

Shoji, T. ;

Wang, J. Q. ;

Han, E. -H. ;

Ke, W. .

CORROSION SCIENCE, 2011, 53 (03) :1137-1142

[22] Residual strain measurement and grain boundary characterization in the heat-affected zone of a weld joint between Alloy 690TT and Alloy 52 [J].

Hou, J. ;

Shoji, T. ;

Lu, Z. P. ;

Peng, Q. J. ;

Wang, J. Q. ;

Han, E. -H. ;

Ke, W. .

JOURNAL OF NUCLEAR MATERIALS, 2010, 397 (1-3) :109-115

[23]

Ilevbare G., 2010, MRP INT C EXH PWR

[24]

Kamada T., 2007, COMMUNICATION 0725

[25] Measurement of local plastic strain distribution of stainless steel by electron backscatter diffraction [J].

Kamaya, Masayuki .

MATERIALS CHARACTERIZATION, 2009, 60 (02) :125-132

[26] Nanoscale characterisation of grain boundary oxidation in cold-worked stainless steels [J].

Kruska, Karen ;

Lozano-Perez, Sergio ;

Saxey, David W. ;

Terachi, Takumi ;

Yamada, Takuyo ;

Smith, George D. W. .

CORROSION SCIENCE, 2012, 63 :225-233

[27]

Kumagai K., 2009, P 14 C ENV DEGR MAT, P671

[28] Stress corrosion cracking of a low alloy steel to stainless steel transition weld in PWR primary waters at 292°C [J].

Li, GF ;

Congleton, J .

CORROSION SCIENCE, 2000, 42 (06) :1005-1021

[29]

MARIN MLC, 2003, P 11 INT S ENV DEGR, P845

[30]

*NISA, 2008, CRACKS INN SURF WELD

← 1 2 3 4 5 →