Stress corrosion cracking in the heat affected zone of a stainless steel 308L-316L weld joint in primary water

被引：65
|
作者：
Dong, Lijin [1 ,2 ]
Peng, Qunjia [1 ]
Han, En-Hou [1 ]
Ke, Wei [1 ]
Wang, Lei [2 ]
机构：
[1] Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China
[2] Northeastern Univ, Key Lab Anisotropy & Texture Mat, Minist Educ, Shenyang 110819, Peoples R China
来源：
CORROSION SCIENCE | 2016年 / 107卷
基金：
中国国家自然科学基金;
关键词：
Stainless steel; SEM; TEM; Stress corrosion; Welding; HIGH-TEMPERATURE WATER; PWR PRIMARY WATER; LOW-ALLOY STEEL; GROWTH; MICROSTRUCTURE; ENVIRONMENT; CHEMISTRY; REGION; 690TT;
D O I：
10.1016/j.corsci.2016.02.030
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Stress corrosion cracking (SCC) in the heat affected zone (HAZ) of a stainless steel 308L-316L weld joint in primary water of pressurized water reactor was investigated. Stress corrosion crack growth in the HAZ was observed in off-normal primary water chemistry with dissolved oxygen, but not in normal primary water chemistry with dissolved hydrogen. This suggests that it is unlikely a stress corrosion crack propagating in the HAZ could reach the fusion boundary and penetrate into the weld metal under normal primary water chemistry conditions. Microstructure analysis of the crack tip suggests that the SCC follows the slip-oxidation mechanism. (C) 2016 Elsevier Ltd. All rights reserved.
引用
收藏
页码：172 / 181
页数：10
相关论文
共 50 条
  • [1] Microstructure and corrosion behavior of the heat affected zone of a stainless steel 308L-316L weld joint
    Cheng Ma
    Qunjia Peng
    Jinna Mei
    En-Hou Han
    Wei Ke
    Journal of Materials Science & Technology, 2018, 34 (10) : 1823 - 1834
  • [2] Microstructure and corrosion behavior of the heat affected zone of a stainless steel 308L-316L weld joint
    Ma, Cheng
    Peng, Qunjia
    Mei, Jinna
    Han, En-Hou
    Ke, Wei
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2018, 34 (10) : 1823 - 1834
  • [3] Microstructure and stress corrosion cracking of a SA508-309L/308L-316L dissimilar metal weld joint in primary pressurized water reactor environment
    Dong, Lijin
    Ma, Cheng
    Peng, Qunjia
    Han, En-Hou
    Ke, Wei
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2020, 40 : 1 - 14
  • [4] Stress corrosion cracking of 316L HAZ for 316L stainless steel/Inconel 52M dissimilar metal weld joint in simulated primary water
    Zhu, Ruolin
    Wang, Jianqiu
    Zhang, Litao
    Zhang, Zhiming
    Han, En-hou
    CORROSION SCIENCE, 2016, 112 : 373 - 384
  • [5] Microstructure and stress corrosion cracking of a SA508-309L/308L-316L dissimilar metal weld joint in primary pressurized water reactor environment
    Lijin Dong
    Cheng Ma
    Qunjia Peng
    En-Hou Han
    Wei Ke
    JournalofMaterialsScience&Technology, 2020, 40 (05) : 1 - 14
  • [6] The Pitting Corrosion Behavior of the Austenitic Stainless Steel 308L-316L Welded Joint
    He, Jinshan
    Xu, Shiguang
    Ti, Wenxin
    Han, Yaolei
    Mei, Jinna
    Wang, Xitao
    METALS, 2020, 10 (09) : 1 - 12
  • [7] Environmentally assisted crack growth in 308L stainless steel weld metal in simulated primary water
    Dong, Lijin
    Han, En-Hou
    Peng, Qunjia
    Ke, Wei
    Wang, Lei
    CORROSION SCIENCE, 2017, 117 : 1 - 10
  • [8] Characterization of microstructure and local deformation in 316NG weld heat-affected zone and stress corrosion cracking in high temperature water
    Lu, Zhanpeng
    Shoji, Tetsuo
    Meng, Fanjiang
    Xue, He
    Qiu, Yubing
    Takeda, Yoichi
    Negishi, Koji
    CORROSION SCIENCE, 2011, 53 (05) : 1916 - 1932
  • [9] Differences of corrosion fatigue behaviors among 316LN base metal, 316LN heat-affected zone and 308L weld metal in a safe-end weld joint in borated and lithiated high-temperature water
    Gao, Jun
    Zhang, Ziyu
    Tan, Jibo
    Wu, Xinqiang
    Wang, Xiang
    Han, En-Hou
    Ke, Wei
    INTERNATIONAL JOURNAL OF FATIGUE, 2021, 148
  • [10] Correlating oxidation resistance to stress corrosion cracking of 309L and 308L stainless steel claddings in simulated PWR primary water
    Cui, Tongming
    Xu, Xinhe
    Pan, Deng
    Lu, Zhanpeng
    Ma, Jiarong
    Yang, Shuangliang
    Zheng, Hui
    Zhong, Zhimin
    Shoji, Tetsuo
    JOURNAL OF NUCLEAR MATERIALS, 2022, 561
12345