EIS analysis on the corrosion resistance of X80 steel under AC interference in simulated soil solution

被引:4
作者
Li, Zhong [1 ]
Sun, Baozhuang [2 ]
Pan, Yue [2 ]
Huang, Liang [2 ]
机构
[1] Chinese Soc Corros & Protect, CSCP, Beijing 100083, Peoples R China
[2] Univ Sci & Technol Beijing, Minist Educ, Corros & Protect Ctr, Key Lab Corros & Protect, Beijing 100083, Peoples R China
来源
INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE | 2021年 / 16卷 / 06期
关键词
AC corrosion; pipeline steel; EIS; charge transfer resistance; ALTERNATING-CURRENT; CRACKING BEHAVIOR; PIPELINE STEEL; CATHODIC PROTECTION; MECHANISTIC ASPECT; CURRENT-DENSITY; CARBON-STEEL; MILD-STEEL; VOLTAGE;
D O I
10.20964/2021.06.08
中图分类号
O646 [电化学、电解、磁化学];
学科分类号
081704 ;
摘要
In this work, the corrosion mechanism of X80 steel under AC interference was studied with electrochemical measurements. The surface potential was monitored at various AC current densities. EIS (electrochemical impedance spectroscopy) measurements were conducted at various AC voltage amplitudes and for various time durations. Variations in the modulus values of the real part and imaginary part were studied. In addition, to simplify the problem, EIS was measured under the effect of various DC potentials. The surface potential was of the same frequency as the AC interference, and the amplitude of the electrode surface potential was linear with the applied current density. As the AC current density increased, the charge transfer resistance decreased due to the acceleration of both the anodic and cathodic processes. When the AC current density reached a certain value, hydrogen and oxygen evolution occurred because the effective Faraday potential exceeded the corresponding critical reaction potential. With an increasing AC time, the charge transfer resistance increased, which was due to the formation of a protective corrosion product film. With the application of low-amplitude AC voltages, there was only a small change in the capacitance of the electric double layer. Nevertheless, with the application of AC voltages at higher amplitudes, the modulus values of the real and imaginary parts of EIS were all less rapid, and the ratio of the imaginary part and real part decreased.
引用
收藏
页码:1 / 13
页数:13
相关论文
共 50 条
[41]   Influence of Temperature on the Corrosion Behavior of X80 Steel in an Acidic Soil Environment [J].
Wu, Yuanhui ;
Luo, Suxing ;
Mou, Qingsong .
INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2020, 15 (01) :576-586
[42]   X80 Steel Corrosion Induced by Alternating Current in Water-Saturated Acidic Soil [J].
Wei, Boxin ;
Qin, Qingyu ;
Fu, Qi ;
Bai, Yunlong ;
Xu, Jin ;
Yu, Changkun ;
Sun, Cheng ;
Ke, Wei .
CORROSION, 2020, 76 (03) :248-267
[43]   Tetrahydroacridines as corrosion inhibitor for X80 steel corrosion in simulated acidic oilfield water [J].
Zhang, Weiwei ;
Li, Hui-Jing ;
Wang, Meirong ;
Wang, Li-Juan ;
Pan, Qianwen ;
Ji, Xubiao ;
Qin, Yaqian ;
Wu, Yan-Chao .
JOURNAL OF MOLECULAR LIQUIDS, 2019, 293
[44]   The AC corrosion and SCC mechanism of X80 pipeline steel in near-neutral pH solution [J].
Wan, Hongxia ;
Song, Dongdong ;
Cai, Yong ;
Du, Cuiwei .
ENGINEERING FAILURE ANALYSIS, 2020, 118 (118)
[45]   Synergistic effect of sulfate-reducing bacteria and elastic stress on corrosion of X80 steel in soil solution [J].
Wu, Tangqing ;
Xu, Jin ;
Yan, Maocheng ;
Sun, Cheng ;
Yu, Changkun ;
Ke, Wei .
CORROSION SCIENCE, 2014, 83 :38-47
[46]   Crevice corrosion of X80 carbon steel induced by sulfate reducing bacteria in simulated seawater [J].
Zhang, Tiansui ;
Wang, Junlei ;
Li, Guangfang ;
Liu, Hongfang .
BIOELECTROCHEMISTRY, 2021, 142
[47]   STRESS CORROSION CRACKING OF X80 PIPELINE STEEL AT COATING DEFECT IN ACIDIC SOIL [J].
Yan Maocheng ;
Yang Shuang ;
Xu Jin ;
Sun Cheng ;
Wu Tangqing ;
Yu Changkun ;
Ke Wei .
ACTA METALLURGICA SINICA, 2016, 52 (09) :1133-1141
[48]   Effect of Alternating Current and Sulfate-Reducing Bacteria on Corrosion of X80 Pipeline Steel in Soil -Extract Solution [J].
Qing, Yongchang ;
Bai, Yunlong ;
Xu, Jin ;
Wu, Tangqing ;
Yan, Maocheng ;
Sun, Cheng .
MATERIALS, 2019, 12 (01)
[49]   Short-period corrosion of X80 pipeline steel induced by AC current in acidic red soil [J].
Wei, Boxin ;
Qin, Qingyu ;
Bai, Yunlong ;
Yu, Changkun ;
Xu, Jin ;
Sun, Cheng ;
Ke, Wei .
ENGINEERING FAILURE ANALYSIS, 2019, 105 :156-175
[50]   Effect of applied potential on stress corrosion cracking behavior of X80 steel in alkaline soil simulated solution with sulfate-reducing bacteria [J].
Wang, Zeqi ;
Xie, Fei ;
Wang, Dan ;
Liu, Jiaqi .
ENGINEERING FAILURE ANALYSIS, 2021, 121