Effects of microstructure on inverse fracture occurring during drop-weight tear testing of high-toughness X70 pipeline steels

被引:32
作者
Hwang, B [1 ]
Kim, YG
Lee, S
Kim, NJ
Yoo, JY
机构
[1] Pohang Univ Sci & Technol, Ctr Adv Aerosp Mat, Pohang 790784, South Korea
[2] Pohang Univ Sci & Technol, Ctr Adv Aerosp Mat, Pohang, South Korea
[3] Pohang Univ Sci & Technol, Dept Mat Sci & Engn, Pohang, South Korea
来源
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 2005年 / 36A卷 / 02期
关键词
D O I
10.1007/s11661-005-0309-7
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The effects of microstructure on inverse fracture occurring in the hammer-impacted region were analyzed after conducting a drop-weight tear test (DWTT) on high-toughness pipeline steels. Three kinds of steels were fabricated by varying the alloying elements, and their microstructures were varied by the rolling conditions. The pressed-notch (PN) or chevron-notch (CN) DWTT and Charpy V-notch (CVN) impact tests were conducted on the rolled steel specimens, and the results were discussed in comparison with the data obtained from CVN tests of prestrained. specimens. In the hammer-impacted region of the DWTT specimens, abnormal inverse fracture having a cleavage fracture mode appeared, and the inverse fracture area correlated well with the upper-shelf energy (USE) obtained from the CVN test and with the grain size. The steel specimens having a higher USE or having coarse polygonal ferrite tended to have a larger inverse fracture area than those having a lower USE or having fine acicular ferrite. This was because steels having a higher impact absorption energy required higher energy for fracture initiation and propagation during the DWTT. These results were confirmed by the CVN data of prestrained steel specimens.
引用
收藏
页码:371 / 387
页数:17
相关论文
共 41 条
[1]  
Anderson TL., 1994, FRACTURE MECH FUNDAM, P41
[2]  
[Anonymous], 1996, API REC PRACT 5L3
[3]  
[Anonymous], 1975, ASTM STAND NEWS
[4]  
*ASTM, 2002, E2302 ASTM
[5]  
CHUNG JS, 2003, P 13 INT OFFSH POL E
[6]  
De AK, 2003, ADV MATER PROCESS, V161, P27
[7]  
DENYS R, 2000, P 3 INT PIP TECHN C, V1
[8]  
Dieter G.E, 1976, Mechanical Metallurgy
[9]  
Ellwood J.R., 2000, P 2000 INT PIP C ASM
[10]  
HAYASHI T, 1997, C P MAT SOL 97 ACC C, P93