Preparation of the initial solid-liquid interface and melt in directional solidification of Al-18 at%Ni peritectic alloy

被引:27
作者
Su, Yanqing [1 ]
Liu, Dongmei [1 ]
Li, Xinzhong [1 ]
Luo, Liangshu [1 ]
Guo, Jingjie [1 ]
Fu, Hengzhi [1 ]
机构
[1] Harbin Inst Technol, Sch Mat Sci & Engn, Harbin 150001, Peoples R China
基金
中国国家自然科学基金;
关键词
Directional solidification; Initial solid-liquid interface; Thermal stabilization; Peritectic; TEMPERATURE-GRADIENT; MICROSTRUCTURE SELECTION; PHASE; SYSTEMS;
D O I
10.1016/j.jcrysgro.2010.05.018
中图分类号
O7 [晶体学];
学科分类号
0702 ; 070205 ; 0703 ; 080501 ;
摘要
The preparation of the initial solid-liquid interface and melt is a critical step in directional solidification process. Experiments on Al-18 at%Ni peritectic alloy consisting of melting followed by thermal stabilization ranging from 0 to 2 h were carried out in a Bridgman-type furnace. In the directional melting process, due to the temperature gradient imposed on the rod, a mushy zone was created between the complete liquid zone and non-molten solid zone parallel to the temperature gradient. With the thermal stabilization time increase, the volume fraction of the liquid inclusions in the mushy zone decreased. After 2 h of thermal stabilization, the initial solid-liquid interface was corrugated, and the Ni concentration in the complete liquid melt zone was uniform but below the original composition. A solute diffusion transport model in a temperature gradient was proposed to describe the concentration evolution both in the mushy zone and the complete liquid melt zone during thermal stabilization. (C) 2010 Elsevier B.V All rights reserved.
引用
收藏
页码:2441 / 2448
页数:8
相关论文
共 21 条
[1]   MELTING DURING SOLIDIFICATION [J].
ALLEN, DJ ;
HUNT, JD .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1976, 7 (05) :767-770
[2]   Solidification microstructures and solid-state parallels: Recent developments, future directions [J].
Asta, M. ;
Beckermann, C. ;
Karma, A. ;
Kurz, W. ;
Napolitano, R. ;
Plapp, M. ;
Purdy, G. ;
Rappaz, M. ;
Trivedi, R. .
ACTA MATERIALIA, 2009, 57 (04) :941-971
[3]   THE FORMATION OF SOLUTE DEPLETED BANDS IN ALUMINUM GOLD-ALLOYS [J].
BEECH, J .
JOURNAL OF CRYSTAL GROWTH, 1984, 67 (02) :385-390
[4]   Initial transients during solid/liquid phase transformations in a temperature gradient [J].
Bosenberg, U. ;
Buchmann, M. ;
Rettenmayr, M. .
JOURNAL OF CRYSTAL GROWTH, 2007, 304 (01) :281-286
[5]   Microstructure evolution during melting and resolidification in a temperature gradient [J].
Buchmann, M ;
Rettenmayr, M .
JOURNAL OF CRYSTAL GROWTH, 2005, 284 (3-4) :544-553
[6]   Melting of a peritectic phase [J].
Hillert, M ;
Höglund, L .
SCRIPTA MATERIALIA, 2004, 50 (07) :1055-1059
[7]   Phase and microstructure selection in peritectic alloys close to the limit of constitutional undercooling [J].
Hunziker, O ;
Vandyoussefi, M ;
Kurz, W .
ACTA MATERIALIA, 1998, 46 (18) :6325-6336
[8]   Synchrotron microradiography of temperature gradient zone melting in directional solidification [J].
B. Li ;
H. D. Brody ;
A. Kazimirov .
Metallurgical and Materials Transactions A, 2006, 37 (3) :1039-1044
[9]   Two-phase microstructure selection in peritectic solidification: from island banding to coupled growth [J].
Lo, TS ;
Dobler, S ;
Plapp, M ;
Karma, A ;
Kurz, W .
ACTA MATERIALIA, 2003, 51 (03) :599-611
[10]   TEMPERATURE-GRADIENT ZONE-MELTING - APPROACH TO STEADY-STATE [J].
LOGRASSO, TA ;
HELLAWELL, A .
JOURNAL OF CRYSTAL GROWTH, 1984, 66 (03) :531-540