Thermal transformations in mechanically alloyed Fe-Zn-Si materials

被引:2
作者
Uwakweh, O [1 ]
Jordan, A
Maziasz, P
机构
[1] Univ Cincinnati, Dept Mat Sci & Engn, Cincinnati, OH 45221 USA
[2] Oak Ridge Natl Lab, Alloy Behav & Design Grp, Div Met & Ceram, Oak Ridge, TN 37831 USA
来源
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 2000年 / 31卷 / 11期
基金
美国能源部;
关键词
D O I
10.1007/BF02830334
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The ball milling of elemental powders corresponding to Gamma (Fe3Zn10) + 0.12 wt pet Si; Gamma (1) (Fe5Zn21) + 0.12 wt pet Si; delta (FeZn7) + 0.12 wt pet Si; and zeta (FeZn13) + 0.12 wt pet Si composition ratios yields crystalline, mechanically alloyed phases. Differential scanning calorimetry (DSC) measurements of these materials show that they evolve differently, with well-defined characteristic stages. The activation energies for processes corresponding to these stages, based on kinetic analyses, are determined and correlated to microstructural evolvements. The processes occurring during the first stage below 250 degreesC, for all of the materials studied using X-ray diffraction (XRD) analysis, are associated with release of strain, recovery, and limited atomic diffusion. The activation energies for recovery processes are 120 kJ/mole for the Gamma + 0.12 wt pet Si, 131 kJ/mole for delta + 0.12 wt pet Si, and 96 kJ/mole for zeta + 0.12 wt pet Si alloys. At higher temperatures, recrystallization and other structural transformations occur with activation energies of 130 and 278 kJ/mole for Gamma + 0.12 wt % Si; of 161 kJ/mole for Gamma (1) + 0.12 wt pet Si; of 167 and 244 kJ/mole for delta + 0.12 wt pet Si; and of 641 kJ/mole for the zeta + 0.12 wt pet Si. In addition, a eutectic reaction at 420 degreesC +/- 3 degreesC, corresponding to the Zn-Si system, and a melting of Zn in Fe-Zn systems are observed for the zeta + 0.12 wt pet Si material. The relation of FeSi formation in the Sandelin process is discussed.
引用
收藏
页码:2747 / 2754
页数:8
相关论文
共 32 条
[1]   PREPARATION OF TI-BASE INTERMETALLIC COMPOUNDS BY MECHANICAL ALLOYING [J].
AHN, JH ;
LEE, KY .
MATERIALS TRANSACTIONS JIM, 1995, 36 (02) :297-304
[2]  
BARHANTAVAKOLI A, 1985, Z METALLKD, V76, P37
[3]  
CHAKKINGAL U, 1992, P ADV COAT TECHN C N, P3
[4]  
CHEN ZW, 1992, JOM JAN, P22
[5]   CHARACTERIZATION OF HIGH-TEMPERATURE HOT DIP GALVANIZED COATINGS [J].
CHIDAMBARAM, PR ;
RANGARAJAN, V ;
VANOOIJ, WJ .
SURFACE & COATINGS TECHNOLOGY, 1991, 46 (03) :245-253
[6]   DISCONTINUOUS COARSENING AND DISSOLUTION IN AN FE-13.5AT PERCENT ZN SOLID-SOLUTION [J].
CHUANG, TH ;
GUST, W ;
PREDEL, B ;
FOURNELLE, RA .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1989, 112 :175-183
[7]  
Cook D.C., 1993, ZM403 ILZRO
[8]  
GU M, 1991, PLATING SURFACE JAN, P77
[9]   REACTIVITY OF SILICON STEELS IN HOT-DIP GALVANIZING [J].
GUTTMAN, H ;
NIESSEN, P .
CANADIAN METALLURGICAL QUARTERLY, 1972, 11 (04) :609-615
[10]  
*INT CTR DIFFR DAT, 32478 JCPDS INT CTR