Electrochemical passivation of ordered NiAl

被引:14
作者
Lillard, RS [1 ]
Scully, JR [1 ]
机构
[1] Univ Virginia, Dept Mat Sci & Engn, Ctr Electrochem Sci & Engn, Charlottesville, VA 22903 USA
关键词
D O I
10.1149/1.1838593
中图分类号
O646 [电化学、电解、磁化学];
学科分类号
081704 ;
摘要
The passivity and electrochemical behavior of single crystalline, ordered NiAl intermetallic compound in buffered solutions of pH 2, 7, and 12.5 was compared to that of polycrystalline Ni and Al. NiAl exhibited improved passivity compared to Ni at a pH of 2, and improved passivity compared to Al at pH 12.5. Water oxidation and reduction were enhanced on NiAl compared to Al, suggesting the presence of a more conductive or catalytic oxide film. Al2O3 was preferentially formed (> 60 atom % of all oxidized Ni and Al species) throughout the interior of oxide films formed anodically at each pH as well as within the air-formed oxide grown at room temperature. However, the oxide surface layers exhibited a tendency toward nearly equal presence of oxidized Ni+2, especially as the pH was increased to 7 and 12.5. Therefore, Al2O3 formation was favored, but not exclusively, during electrochemical passivation. In contrast, little or no Ni+2 las NiO or NiAl2O4) has been reported after high temperature oxidation of NiAl. The composition of the electrochemically grown oxide is influenced by the specific oxide solubility and kinetic formation/dissolution rates at the oxide/solution interface as well. as by the free energy of formation of the oxides.
引用
收藏
页码:2024 / 2032
页数:9
相关论文
共 35 条
[1]   INITIAL-STAGES OF OXIDATION OF THE NI3AL ALLOY - A STUDY BY X-RAY PHOTOELECTRON-SPECTROSCOPY AND LOW-ENERGY HE+ SCATTERING [J].
BARDI, U ;
ATREI, A ;
ROVIDA, G .
SURFACE SCIENCE, 1990, 239 (1-2) :L511-L516
[2]   INITIAL-STAGES OF OXIDATION OF THE NI3AL ALLOY - STRUCTURE AND COMPOSITION OF THE ALUMINUM-OXIDE OVERLAYER STUDIED BY XPS, LEIS AND LEED [J].
BARDI, U ;
ATREI, A ;
ROVIDA, G .
SURFACE SCIENCE, 1992, 268 (1-3) :87-97
[3]  
BLANKENSHIP CP, 1993, 93CRD199 GEN EL CORP
[4]  
BOUMAN R, 1973, SURF SCI, V35, P8
[5]  
DELGASS WN, 1970, CATALY REV, V4, P179
[6]  
DOYCHAK JK, 1984, P INT C METALL CORRO, V1, P35
[7]   A combined electrochemical and xps study on the passivity of B2 iron aluminides in sulphuric acid solution [J].
Frangini, S ;
DeCristofaro, NB ;
Mignone, A ;
Lascovich, J ;
Giorgi, R .
CORROSION SCIENCE, 1997, 39 (08) :1431-1442
[8]   ELECTRONIC-STRUCTURE OF NI AND PD ALLOYS .2. X-RAY PHOTOELECTRON CORE-LEVEL SPECTRA [J].
HILLEBRECHT, FU ;
FUGGLE, JC ;
BENNETT, PA ;
ZOLNIEREK, Z ;
FREIBURG, C .
PHYSICAL REVIEW B, 1983, 27 (04) :2179-2193
[9]   OXIDATION OF INTERMETALLIC COMPOUND NIAL [J].
HUTCHINGS, R ;
LORETTO, MH ;
SMALLMAN, RE .
METAL SCIENCE, 1981, 15 (01) :7-13
[10]   ESCA STUDIES OF METAL-OXYGEN SURFACES USING ARGON AND OXYGEN ION-BOMBARDMENT [J].
KIM, KS ;
BAITINGER, WE ;
AMY, JW ;
WINOGRAD, N .
JOURNAL OF ELECTRON SPECTROSCOPY AND RELATED PHENOMENA, 1974, 5 (NOV-D) :351-367