Mechanical and Durability Properties of Latex-Modified Hybrid Fiber-Reinforced Roller-Compacted Rapid-Set Cement Concrete for Pavement Repair

This study evaluated the mechanical properties and durability performance of latex-modified hybrid fiber-reinforced roller-compacted rapid-set cement concrete (LMHFRCRSC) for emergency repair of concrete pavement. Experimental parameters included the blend ratio of the hybrid fiber, which comprised natural jute fiber (0-0.2 vol.%) and structural synthetic fiber (0-2 vol.%). The mechanical performance of LMHFRCRSC of various blend ratios was evaluated in terms of compressive, flexural, and splitting tensile strength. Durability assessment included chlorine ion penetration and abrasion resistance measurements. Compressive and flexural strength values of 21 and 3.5 MPa, respectively, were the set targets after 4 h of curing; a compressive strength of 35 MPa, a flexural strength of 4.5 MPa, a splitting tensile strength of 4.2 MPa, and chloride ion penetration of 2000 C or less were required after 28 days of curing. Our test results confirmed that all mix proportions satisfied the target values, regardless of the blend ratio of the hybrid fiber. Specifically, the mechanical performance of the concrete improved as the blend ratio of the structural synthetic fiber increased. With regard to durability, a greater amount of jute fiber, a hydrophilic fiber, enhanced the concrete's durability. Additionally, incorporating jute fiber of 0.6 kg/m(3) provided excellent chlorine ion penetration resistance. The optimal blend ratio for the hybrid fiber was natural jute fiber at 0.6 kg/m(3) and structural synthetic fiber at 13.65 kg/m(3) (mix: J0.6 + P13.65); with this mix proportion, a chloride ion penetration amount of 1000 C or less and maximum mechanical performance were achieved.