Crevice Corrosion Resistance and Structure of Passive Film on Fe-Mn-Si-Cr-Ni Steel

被引：2

作者：

Nishimura, Toshiyasu ^{[1
]}

机构：

[1] Natl Inst Mat Sci, 1-2-1 Sengen, Tsukuba, Ibaraki 3050047, Japan

来源：

ISIJ INTERNATIONAL | 2016年 / 56卷 / 04期

关键词：

shape memory alloy; crevice corrosion; transmission electron microscopy; SHAPE-MEMORY ALLOY; WET/DRY ENVIRONMENT; CARBON-STEEL; BEHAVIOR; TRANSFORMATION; OXIDES;

D O I：

10.2355/isijinternational.ISIJINT-2015-634

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The crevice corrosion resistance of an Fe-Mn-Si-Cr-Ni (15 Mn) steel as a shape memory alloy was estimated by laser microscopy and statistical calculation of the corrosion depth, and the structure of the passive film formed on the steel was examined by EELS (Electron Energy Loss Spectroscopy) analysis using TEM (transmission electron microscopy). The crevice corrosion results were analyzed using a Gumbel distribution, and the mode (lambda) and distribution parameter (alpha) of the maximum corrosion depth of the 15 Mn steel were found to be much smaller than those of 430 stainless steel (SUS: 16Cr - Fe). This shows that 15 Mn steel has a higher crevice corrosion resistance than 430 SUS steel. In AES and XPS analysis, the passive film of 15 Mn steel was shown to contain Fe, Mn, Cr, Si and Ni. From TEM-EELS, the passive film was found to consist of 2 layers. In the passive film, Cr and Si are thought to be effective early, with Ni preventing penetration of crevice corrosion. It was found that 15 Mn steel could maintain a passive film which was composed of effective elements in a crevice corrosion environment.

引用

页码：654 / 660

页数：7

共 24 条

[1]

CHANG LC, 1951, T AM I MIN MET ENG, V191, P47

[2] Determination of chromium valence over the range Cr(0)-Cr(VI) by electron energy loss spectroscopy [J].

Daulton, Tyrone L. ;

Little, Brenda J. .

ULTRAMICROSCOPY, 2006, 106 (07) :561-573

[3] Improvement of oxidation resistance of an Fe-Mn-Si-Cr shape memory alloy by annealing under vacuum [J].

Fukai, H ;

Suzuki, S ;

Masahashi, N ;

Hanada, S ;

Maruyama, T ;

Kubo, H ;

Waseda, Y .

MATERIALS TRANSACTIONS, 2005, 46 (08) :1745-1748

[4] High resolution electron energy loss spectroscopy of manganese oxides: Application to Mn3O4 nanoparticles [J].

Laffont, L. ;

Gibot, P. .

MATERIALS CHARACTERIZATION, 2010, 61 (11) :1268-1273

[5] DEVELOPMENT OF SHAPE MEMORY ALLOYS [J].

MIYAZAKI, S ;

OTSUKA, K .

ISIJ INTERNATIONAL, 1989, 29 (05) :353-377

[6] Structure of the Passive Film formed on Fe-Mn-Si-Cr-Ni Shape Memory Alloy after Wet and Dry Corrosion Test [J].

Nishimura, T. .

MATERIALS TRANSACTIONS, 2014, 55 (06) :871-876

[7] Electrochemical behaviour and structure of rust formed on Si- and Al-bearing steel after atmospheric exposure [J].

Nishimura, T. .

CORROSION SCIENCE, 2010, 52 (11) :3609-3614

[8] Electrochemical behavior of rust formed on carbon steel in a wet/dry environment containing chloride ions [J].

Nishimura, T ;

Katayama, H ;

Noda, K ;

Kodama, T .

CORROSION, 2000, 56 (09) :935-941

[9] Corrosion Behavior of silicon-bearing steel in a wet/dry environment containing chloride ions [J].

Nishimura, Toshiyasu .

MATERIALS TRANSACTIONS, 2007, 48 (06) :1438-1443

[10] Acetic Acid Vapor Corrosion of Lead-Tin Alloys Containing 3.4 and 15% Tin [J].

Oertel, Catherine M. ;

Baker, Shefford P. ;

Niklasson, Annika ;

Johansson, Lars-Gunnar ;

Svensson, Jan-Erik .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2009, 156 (12) :C414-C421

← 1 2 3 →