Annealing Temperature Dependence of ZTO Thin Film Properties and Its Application on Thin Film Transistors by Inkjet Printing

被引：11
|
作者：
Ryu, Sang Ouk [1 ]
Ha, Cheul Ho [2 ]
Jun, Ho Young [2 ]
Ryu, Si Ok [2 ]
机构：
[1] Dankook Univ, Dept Elect & Elect Engn, Yongin 16890, South Korea
[2] Yeungnam Univ, Sch Chem Engn, Gyongsan 38541, South Korea
来源：
JOURNAL OF ELECTRONIC MATERIALS | 2020年 / 49卷 / 03期
关键词：
Zinc tin oxide; thin film; thin film transistor; inkjet-printer; solution-based process; FABRICATION;
D O I：
10.1007/s11664-019-07871-7
中图分类号：
TM [电工技术]; TN [电子技术、通信技术];
学科分类号：
0808 ; 0809 ;
摘要：
In this study, inkjet-printed zinc tin oxide:Cl (ZTO:Cl) thin films were analyzed using x-ray diffraction, x-ray photoelectron spectroscopy (XPS) and all the films were annealed at temperatures ranging from 100 degrees C to 600 degrees C. XPS analysis showed that the formation of metal-oxide bonds in the films was complete with annealing temperatures at or above 500 degrees C. Furthermore, inkjet-printed thin film transistors (TFTs) were examined using scanning electron microscopy and current-voltage characteristic measurements. The ZTO:Cl TFTs performed best when annealed at 500 degrees C. The average carrier mobility and the on/off ratio were found to be 2.71 cm(2)/V s and 1.82x10(7), respectively.
引用
收藏
页码：2003 / 2007
页数：5
相关论文
共 50 条
  • [41] Printed low temperature metal oxide thin film transistors
    Chen, Z.
    Wu, X. Z.
    Zhou, T.
    Cui, Z.
    2014 9TH IEEE INTERNATIONAL CONFERENCE ON NANO/MICRO ENGINEERED AND MOLECULAR SYSTEMS (NEMS), 2014, : 422 - 425
  • [42] Effect Of Channel Layer Thickness On The Performance Of Indium-Zinc-Tin Oxide Thin Film Transistors Manufactured By Inkjet Printing
    Avis, Christophe
    Hwang, Hye Rim
    Jang, Jin
    ACS APPLIED MATERIALS & INTERFACES, 2014, 6 (14) : 10941 - 10945
  • [43] In2O3 Thin-Film Transistors via Inkjet Printing for Depletion-Load nMOS Inverters
    Leppaniemi, J.
    Eiroma, K.
    Majumdar, H. S.
    Alastalo, A.
    IEEE ELECTRON DEVICE LETTERS, 2016, 37 (04) : 445 - 448
  • [44] Dielectric optimization for Inkjet-Printed TIPSPentacene Organic Thin-Film Transistors
    Singh, Subhash
    Mohapatra, Y. N.
    2014 IEEE 2ND INTERNATIONAL CONFERENCE ON EMERGING ELECTRONICS (ICEE), 2014,
  • [45] Low-temperature solution-processed InGaZnO thin film transistors by using lightwave-derived annealing
    Zhang, Qian
    Ruan, Cheng
    Xia, Guodong
    Gong, Hongyu
    Wang, Sumei
    THIN SOLID FILMS, 2021, 723
  • [46] A new nanocomposite dielectric ink and its application in printed thin-film transistors
    Wu, Xinzhou
    Fei, Fei
    Chen, Zheng
    Su, Wenming
    Cui, Zheng
    COMPOSITES SCIENCE AND TECHNOLOGY, 2014, 94 : 117 - 122
  • [47] The effects of deposition conditions and annealing temperature on the performance of gallium tin zinc oxide thin film transistors
    Bradley, Tanina
    Iyer, Shanthi
    Alston, Robert
    Collis, Ward
    Lewis, Jay
    Cunningham, Garry
    Forsythe, Eric
    OXIDE-BASED MATERIALS AND DEVICES IV, 2013, 8626
  • [48] Hydrogenated polycrystalline SiGe films and their application in Thin Film Transistors
    Rodríguez, A
    Rodríguez, T
    Sangrador, J
    San Andrés, E
    Mártil, I
    BOLETIN DE LA SOCIEDAD ESPANOLA DE CERAMICA Y VIDRIO, 2004, 43 (02): : 386 - 389
  • [49] Influence of indium doping on the properties of zinc tin oxide films and its application to transparent thin film transistors
    Choi, Mu Hee
    Ma, Tae Young
    THIN SOLID FILMS, 2014, 550 : 654 - 659
  • [50] Amorphous LaZnSnO thin films by a combustion solution process and application in thin film transistors
    Jun Li
    Chuan-Xin Huang
    Yi-Zhou Fu
    Jian-Hua Zhang
    Xue-Yin Jiang
    Zhi-Lin Zhang
    Electronic Materials Letters, 2016, 12 : 76 - 81
12345