Research of annealing influence on the hardness of detonation coatings from aluminum oxide

The article examines the effect of annealing on the structure and properties of alumina-based coatings obtained by detonation spraying. Coated samples were kept separately at temperatures of 500, 700, 800 and 1200 degrees C at a pressure of 3.6*10(-4) Pa for more than 1 hour. It was found that the microhardness of coatings made of alumina increases by 15-30 % after annealing depending on annealing temperature. The results of nanoindentation show that at 1200 degrees C the nanohardness of coatings after annealing increases by almost 100%. Aluminum oxide coating is characterized by high strength and density of the coating before and after annealing, and slight porosity. Results of X-ray analysis showed that the alumina powder consists of alpha-Al2O3 lattice, and after detonation injection coating cubes are converted into a semi-gamma-cubic lattice. It was found that during the annealing of the coating at 1200 degrees C all cells of gamma-phase completely transit to the alpha-phase. It was found that the increase in hardness after annealing of alumina coating at 500, 700, 800 and 1200 degrees C is associated with an increase in volume fraction of alpha-Al2O3 phase.