Synthesis and Properties of Binary Spinels in a NiO-CuO-Fe2O3-Cr2O3 System

The conditions for the formation of a spinel structure from a NiO-CuO-Fe2O3-Cr2O3 oxide mixture using several technological approaches have been examined. Addition of KCl is accompanied with the formation of two spinel-like phases, whereas in the absence of KCl just one solid solution of nickel-copper ferrite-chromite with the structure of a cubic spinel is formed. At the temperature of thermal treatment of 900 degrees C, the presence of an admixture phase of the delafossite (CuCrO2) type was established. The conditions for the fabrication of samples containing two spinel phases (cubic and tetragonal) characterized with the most developed surface and manifesting = increased catalytic activity in the reaction of the decomposition of an organic substance by hydrogen peroxide have been formulated. The studied features of spinel synthesis can be of interest for developing materials with an active surface promising for application as adsorbents of catalysts and sensors.