Feature of flow stress of aluminum sheet used for can during hot compression

The flow stress feature of aluminum sheet used for pressure can during plastic deformation at elevated temperature was studied by isothermal compression test using Gleeble 1500 dynamic materials testing machine. The experimental results show that the steady state deformation is remarkable when the material is deformed in the temperature range of 350 similar to 500 degrees C at strain rates within the range of 10(-2) similar to 10.0s(-1). The material is sensitive to positive strain rate. A hyperbolic sine relationship is found to correlate well the flow stress with the strain rate, and an Arrhenius relationship with the temperature. Semi-empirical constitutive equations of the flow stress are derived from all experimental data for tested material during plastic deformation at elevated temperature by polyelement linear regression analysis.