Structure and Magnetic Properties of Carbon Encapsulated Co Nanoparticles Prepared by the Pyrolysis of Mixture of Sucrose and Cobalt Nitrate

被引：1

作者：

Xue, J. ^{[1
,2
]}

Chen, S. C. ^{[2
]}

Tang, H. K. ^{[2
]}

Xiang, H. K. ^{[2
]}

Wang, X. H. ^{[2
]}

Cao, H. ^{[2
]}

机构：

[1] Wuhan Res Inst Mat Protect, Wuhan 430030, Peoples R China

[2] Wuhan Inst Technol, Sch Mat Sci & Engn, Wuhan 430074, Peoples R China

来源：

MANUFACTURING SCIENCE AND ENGINEERING, PTS 1-5 | 2010年 / 97-101卷

关键词：

Carbon; Cobalt Nanoparticle; Core-shell structure; Pyrolysis; Magnetic property; RAMAN-SCATTERING; GRAPHITE; NANOCRYSTALS; CRYSTALS;

D O I：

10.4028/www.scientific.net/AMR.97-101.2201

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Carbon-encapsulated Cobalt nanoparticles were synthesized with sucrose as carbon source and cobalt nitrate as metal source in nitrogen atmosphere. The weight of purified sample could arrive around 12-20 grams at one time. The as-prepared CECNPs sample was characterized by transmission electron microscopy (TEM), X-ray diffraction technique (XRD), vibrating sample magnetometer (VSM) and Raman spectroscopy. The results showed CECNPs was typical core / shell structure on nanometer scale, the core was cobalt single crystal, the shell was graphitic carbon, and the particle size was about 30nm. The magnetic measurement revealed that CECNPs was ferromagnetic material with the quite small remanent magnetizations Mr of 3.7emu/g and coercive forces He of 275Oe at room temperature.

引用

页码：2201 / +

页数：2

共 17 条

[1] Study of the optical limiting properties of carbon-encapsulated magnetic nanoparticles [J].

Bystrzejewski, M. ;

Lange, H. ;

Huczko, A. ;

Elim, H. I. ;

Ji, W. .

CHEMICAL PHYSICS LETTERS, 2007, 444 (1-3) :113-117

[2] Carbon encapsulated magnetic nanoparticles for biomedical applications: Thermal stability studies [J].

Bystrzejewski, Michal ;

Cudzilo, Stanislaw ;

Huczko, Andrzej ;

Lange, Hubert ;

Soucy, Gervais ;

Cota-Sanchez, German ;

Kaszuwara, Waldemar .

BIOMOLECULAR ENGINEERING, 2007, 24 (05) :555-558

[3] A simple technique for the synthesis of filled carbon nanoparticles [J].

Harris, PJF ;

Tsang, SC .

CHEMICAL PHYSICS LETTERS, 1998, 293 (1-2) :53-58

[4] Magnetic thin films of cobalt nanocrystals encapsulated in graphite-like carbon [J].

Hayashi, T ;

Hirono, S ;

Tomita, M ;

Umemura, S .

NATURE, 1996, 381 (6585) :772-774

[5] Magnetic nanoparticles [J].

Kodama, RH .

JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 1999, 200 (1-3) :359-372

[6] Large-scale preparation of carbon-encapsulated cobalt nanoparticles by the catalytic method [J].

Liu, BH ;

Ding, J ;

Zhong, ZY ;

Dong, ZL ;

White, T ;

Lin, JY .

CHEMICAL PHYSICS LETTERS, 2002, 358 (1-2) :96-102

[7] Carbon-encapsulated Fe nanoparticles from detonation-induced pyrolysis of ferrocene [J].

Lu, Y ;

Zhu, ZP ;

Liu, ZY .

CARBON, 2005, 43 (02) :369-374

[8] 1ST-ORDER AND 2ND-ORDER RAMAN-SCATTERING FROM FINITE-SIZE CRYSTALS OF GRAPHITE [J].

NEMANICH, RJ ;

SOLIN, SA .

PHYSICAL REVIEW B, 1979, 20 (02) :392-401

[9] Synthesis, structures and magnetic properties of carbon-encapsulated nanoparticles via thermal decomposition of metal acetylide [J].

Nishijo, Junichi ;

Okabe, Chie ;

Oishi, Osamu ;

Nishi, Nobuyuki .

CARBON, 2006, 44 (14) :2943-2949

[10] Graphite encapsulation of catalytic metal nanoparticles [J].

Nolan, PE ;

Lynch, DC ;

Cutler, AH .

CARBON, 1996, 34 (06) :817-819

← 1 2 →