Effect of Mo content on microstructure and stress-rupture properties of a Ni-base single crystal superalloy

被引:22
作者
Liang, Yunfei [1 ]
Li, Shusuo [1 ]
Ai, Cheng [1 ]
Han, Yafang [1 ]
Gong, Shengkai [1 ]
机构
[1] Beihang Univ, Sch Mat Sci & Engn, Beijing 100191, Peoples R China
基金
中国博士后科学基金;
关键词
Ni-base single crystal superalloy; Mo content; Stress-rupture property; LAST STAGE SOLIDIFICATION; MECHANICAL-PROPERTIES; CREEP-PROPERTIES; 3RD-GENERATION; PATH;
D O I
10.1016/j.pnsc.2016.01.006
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The additional 1.5 wt% Mo was added in a Ni-base single crystal (SC) alloy with the composition of Ni-6.5A1-8.0Mo-2.4Cr-6.2Ta-4.9Co-1.5Re-(0.01-0.05)Y (wt%) to study the effect of Mo content on the microstructure and stress-rupture properties. The creep and stress-rupture tests under the conditions of 850 degrees C/500 MPa and 1100 degrees C/130 MPa were conducted, and the microstructure of as-cast, heat treated and stress ruptured specimens were analyzed. It was found that the 1.5 wt% Mo addition enhanced the stress-rupture lives at both intermediate (850 degrees C) and high (1100 degrees C) temperatures. The microstructure analysis showed that adding 1.5 wt% Mo in the basic alloy affected the microstructure dramatically, i.e., the Mo-rich phases formed in the specimens of as-cast and stress-ruptured specimens. It is considered that the improvement of the stress-rupture lives is duo to the strengthening effect of Mo to both gamma and gamma' phases and the decrease of stacking fault energy, diffusion constant and dislocation spacing. The Mo-rich phases precipitated under condition of 1100 degrees C/130 MPa did not affect the creep and stress-rupture properties obviously in the present study. (C) 2016 Chinese Materials Research Society. Production and hosting by Elsevier B.V. This is an open access article under the CC BY-NC-ND license (httplicreati ecommons.org/licen,,es/by-nc-ndf4.0).
引用
收藏
页码:112 / 116
页数:5
相关论文
共 15 条
  • [1] Influence of withdrawal rate on last stage solidification path of a Mo-rich Ni3Al based single crystal superalloy
    Ai, Cheng
    Zhao, Xinbao
    Liu, Lei
    Zhang, Heng
    Ru, Yi
    Pei, Yanling
    Zhou, Jian
    Li, Shusuo
    Gong, Shengkai
    [J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2015, 623 : 362 - 366
  • [2] Solidification path in third-generation Ni-based superalloys, with an emphasis on last stage solidification
    D'Souza, N.
    Dong, H. B.
    [J]. SCRIPTA MATERIALIA, 2007, 56 (01) : 41 - 44
  • [3] Donachie M.J., 2002, SUPERALLOYS, V2nd, P1
  • [4] ERICKSON GL, 1995, JOM-J MIN MET MAT S, V47, P36
  • [5] EFFECT OF 900-1150 DEGREES-C AGING ON THE MICROSTRUCTURE AND MECHANICAL-PROPERTIES OF A DS CASTING NI3AL-BASE ALLOY IC6
    HAN, YF
    LI, SH
    JIN, Y
    CHATURVEDI, MC
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1995, 192 : 899 - 907
  • [6] A New Approach of Designing Superalloys for Low Density
    MacKay, R. A.
    Gabb, T. P.
    Smialek, J. L.
    Nathal, M. V.
    [J]. JOM, 2010, 62 (01) : 48 - 54
  • [7] INFLUENCE OF MOLYBDENUM ON THE CREEP-PROPERTIES OF NICKEL-BASE SUPERALLOY SINGLE-CRYSTALS
    MACKAY, RA
    NATHAL, MV
    PEARSON, DD
    [J]. METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1990, 21 (02): : 381 - 388
  • [8] Reed R. C., 2008, SUPERALLOYS FUNDAMEN, P18
  • [9] A Comparative Study of the γ/γ' Eutectic Evolution During the Solidification of Ni-Base Superalloys
    Seo, S. M.
    Lee, J. H.
    Yoo, Y. S.
    Jo, C. Y.
    Miyahara, H.
    Ogi, K.
    [J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2011, 42A (10): : 3150 - 3159
  • [10] MEASUREMENT OF STRUCTURAL PARAMETERS IMPORTANT IN CREEP OF NI-MO AND NI-W SOLID-SOLUTIONS
    TIEARNEY, TC
    GRANT, NJ
    [J]. METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1982, 13 (10): : 1827 - 1836