SYNTHESIS OF MAGNESIUM ALUMINATE SPINEL DOPED TiO2 FROM MAGNESITE WASTE

被引：3

作者：

Canikoglu, N. ^{[1
]}

机构：

[1] Sakarya Univ, Engn Fac, Dept Met & Mat Engn, Sakarya, Turkey

来源：

ARCHIVES OF METALLURGY AND MATERIALS | 2022年 / 67卷 / 01期

关键词：

Magnesium aluminate spinel (MgAl2O4); Titanium dioxide (TiO2); Magnesite waste; Alumina (Al2O3); MGAL2O4; SPINEL; MICROSTRUCTURE; DENSIFICATION; STRENGTH;

D O I：

10.24425/amm.2022.137757

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Magnesium aluminate spinel (MgAl2O4) is an important refractory material of magnesia origin. It is formed by the reaction of magnesium and aluminum oxides. In this study, TiO2 was added to magnesite waste and alumina (Al2O3) powders in different proportions and the mixtures were sintered at different temperatures after shaping. The aim of this study was to produce spinel economically by recycling waste materials. Therefore, titanium dioxide (TiO2) added magnesium aluminate spinel was produced and the products obtained were characterized by XRD and SEM-EDS analyses. In addition, bulk density, apparent porosity and microhardness values were measured and the effects of TiO2 additive on magnesium aluminate properties were examined. The better values were determined in samples doped 4 wt.% TiO2 at the temperature of 1400 degrees C.

引用

页码：311 / 316

页数：6

共 17 条

[11] Effect of addition of Cr2O3 on the properties of reaction sintered MgO-Al2O3 spinels [J].

Sarkar, R ;

Das, SK ;

Banerjee, G .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2002, 22 (08) :1243-1250

[12] Effect of raw materials on formation and densification of magnesium aluminate spinel [J].

Sarkar, Ritwik ;

Sahoo, Sachin .

CERAMICS INTERNATIONAL, 2014, 40 (10) :16719-16725

[13] Role of different rare earth oxides on the reaction sintering of magnesium aluminate spinel [J].

Sinhamahapatra, Somnath ;

Dana, Kausik ;

Mukhopadhyay, Sunanda ;

Tripathi, Himansu Sekhar .

CERAMICS INTERNATIONAL, 2019, 45 (09) :11413-11420

[14] Synthesis and densification behaviour of magnesium aluminate spinel: Effect of Dy2O3 [J].

Tripathi, H. S. ;

Singla, S. ;

Ghosh, A. .

CERAMICS INTERNATIONAL, 2009, 35 (06) :2541-2544

[15]

Ugur P., 2010, THESIS ANADOLU U TUR

[16] Effect of TiO2 addition on microstructure and strength of porous spinel (MgAl2O4) ceramics prepared from magnesite and Al(OH)3 [J].

Yan, Wen ;

Lin, Xiaoli ;

Chen, Junfeng ;

Li, Nan ;

Wei, Yaowu ;

Han, Bingqiang .

JOURNAL OF ALLOYS AND COMPOUNDS, 2015, 618 :287-291

[17] Effect of polymorphism of Al2O3 on the synthesis of magnesium aluminate spinel [J].

Zhang, ZH ;

Li, N .

CERAMICS INTERNATIONAL, 2005, 31 (04) :583-589

← 1 2 →