Electrochemical corrosion of solid and liquid phase sintered silicon carbide in acidic and alkaline environments

被引:31
作者
Andrews, A.
Herrmann, M.
Sephton, M.
Machio, Chr.
Michaelis, A.
机构
[1] Fraunhofer Inst Ceram Technol & Syst, D-01277 Dresden, Germany
[2] Univ Witwatersrand, Sch Chem & Met Engn, ZA-2050 Wits, Johannesburg, South Africa
关键词
LPS SiC; corrosion SiC; electrochemical corrosion;
D O I
10.1016/j.jeurceramsoc.2006.07.011
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Solid and liquid phase sintered silicon carbide (SiC) ceramics are used in aggressive environments, e.g. as seals and linings in chemical plant equipments. There exist data concerning corrosion of solid phase sintered SiC (SSiC), but there are only few data concerning their electrochemical corrosion behaviour. The corrosion of liquid phase sintered SiC ceramics (LPS SiC) containing yttria aluminium oxide grain boundary phases has been investigated by standard methods that have shown the decisive influence of the oxide grain boundary on the corrosion stability of these materials. But no electrochemical investigations are known. In this study therefore, potentiodynamic polarisation measurements have been used to determine the corrosion mechanisms of SSiC and LPS SiC ceramics at room temperature in acidic and alkaline environments. The investigation has shown a pronounced electrochemical corrosion in acids and alkaline solutions for both types of materials. In HCl and HNO3 pseudo-passivity features due to the formation of a thin layer of SiO2 on the surface were observed, whereas in NaOH soluble silicate ions were observed resulting in more pronounced corrosion. Microstructural observations of initial and corroded samples revealed that the residual carbon found in the microstructure of SSiC did not dissolve preferentially. The corrosion current densities of the LIPS SiC materials were caused by the dissolution of SiC and not by the corrosion of the oxide grain boundary phase. The Corrosion current densities of the LPS SiC materials investigated were lower than those of the SSiC materials. (c) 2006 Published by Elsevier Ltd.
引用
收藏
页码:2127 / 2135
页数:9
相关论文
共 19 条
[1]  
Andrews A, 2006, J S AFR I MIN METALL, V106, P269
[2]  
ANDREWS A, 2005, THESIS U WITWATERSRA
[3]  
Antelmann M.S., 1982, ENCY CHEM ELECT POTE, P101
[4]  
*ASTM, 2000, ANN BOOK ASTM STAND, P57
[5]  
ASTM, 2000, ANN BOOK ASTM STAND, V04.08, P38
[6]  
Bard A.J., 1985, ELECTROANALYTICAL CH, P189
[7]   Densification of liquid phase sintered silicon carbide [J].
Can, A ;
Herrmann, M ;
McLachlan, DS ;
Sigalas, I ;
Adler, J .
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2006, 26 (09) :1707-1713
[8]   ELECTROCHEMICAL TECHNIQUES FOR CORROSION RATE DETERMINATION IN CERAMICS [J].
DIVAKAR, R ;
SESHADRI, SG ;
SRINIVASAN, M .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1989, 72 (05) :780-784
[9]  
HERRMANN M, 2003, DKG, V80, pE27
[10]   The influence of porosity on the electrical properties of liquid-phase sintered silicon carbide [J].
Ihle, J. ;
Martin, H. -P. ;
Herrmann, M. ;
Obenaus, P. ;
Adler, J. ;
Hermel, W. ;
Michaelis, A. .
INTERNATIONAL JOURNAL OF MATERIALS RESEARCH, 2006, 97 (05) :649-656