On the Interactions and Synergism between Phases of Carbon-Phosphorus-Titanium Composites Synthetized from Cellulose for the Removal of the Orange-G Dye

Carbon-phosphorus-titanium composites (CPT) were synthesized by Ti-impregnation and carbonization of cellulose. Microcrystalline cellulose used as carbon precursor was initially dissolved by phosphoric acid (H3PO4) to favor the Ti-dispersion and the simultaneous functionalization of the cellulose chains with phosphorus-containing groups, namely phosphates and polyphosphates. These groups interacted with the Ti-precursor during impregnation and determined the interface transformations during carbonization as a function of the Ti-content and carbonization temperature. Amorphous composites with high surface area and mesoporosity were obtained at low Ti-content (Ti:cellulose ratio = 1) and carbonization temperature (500 degrees C), while in composites with Ti:cellulose ratio = 12 and 800 degrees C, Ti-particles reacted with the cellulose groups leading to different Ti-crystalline polyphosphates and a marked loss of the porosity. The efficiency of composites in the removal of the Orange G dye in solution by adsorption and photocatalysis was discussed based on their physicochemical properties. These materials were more active than the benchmark TiO2 material (Degussa P25), showing a clear synergism between phases.