Precipitation of γ′ phases during slow cooling of nickel based superalloy

被引：3

作者：

Liu, Y. ^{[1
]}

Li, S. ^{[1
]}

Pei, Y. ^{[1
]}

Zhang, H. ^{[1
]}

Gong, S. ^{[1
]}

机构：

[1] Beijing Univ Aeronaut & Astronaut, Sch Mat Sci & Engn, Beijing 100191, Peoples R China

来源：

MATERIALS RESEARCH INNOVATIONS | 2014年 / 18卷

关键词：

Nickel based superalloy; Slow cooling process; Precipitation; gamma ' phases; GENERATIONS;

D O I：

10.1179/1432891714Z.000000000708

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In this paper, the precipitation behaviour of gamma' phases during cooling after solution treatment has been investigated. An experimental superalloy with a large gamma' volume fraction was employed, and the average cooling rate was ca. 5 degrees C min(-1). In order to investigate the forming of precipitates at different temperature stages, interrupt quenching was used during the cooling process. As the results show, the gamma' precipitates change from monomodal to multimodal size distributions with quenching temperature. On the one hand, the large gamma' phases were mainly formed by coalescing and merging. On the other hand, small gamma' in the matrix were continuously precipitated during the cooling process, and the nucleation was not shut off until quenching at 1100 degrees C. The precipitation mechanism is also discussed in this paper.

引用

页码：390 / 394

页数：5

共 17 条

[11] Precipitate growth activation energy requirements in the duplex size γ′ distribution in the superalloy IN738LC [J].

Roy, I ;

Balikci, E ;

Ibekwe, S ;

Raman, A .

JOURNAL OF MATERIALS SCIENCE, 2005, 40 (23) :6207-6215

[12] Formation of multimodal size distributions of γ′ in a nickel-base superalloy during interrupted continuous cooling [J].

Sarosi, P. M. ;

Wang, B. ;

Simmons, J. P. ;

Wang, Y. ;

Mills, M. J. .

SCRIPTA MATERIALIA, 2007, 57 (08) :767-770

[13] Microstructure and elevated temperature tensile behaviour of directionally solidified nickel based superalloy [J].

Sheng, L. Y. ;

Yang, F. ;

Xi, T. F. ;

Lai, C. ;

Guo, J. T. .

MATERIALS RESEARCH INNOVATIONS, 2013, 17 :S101-S106

[14] Mechanisms related to different generations of γ′ precipitation during continuous cooling of a nickel base superalloy [J].

Singh, A. R. P. ;

Nag, S. ;

Chattopadhyay, S. ;

Ren, Y. ;

Tiley, J. ;

Viswanathan, G. B. ;

Fraser, H. L. ;

Banerjee, R. .

ACTA MATERIALIA, 2013, 61 (01) :280-293

[15] Influence of cooling rate on the development of multiple generations of γ′ precipitates in a commercial nickel base superalloy [J].

Singh, A. R. P. ;

Nag, S. ;

Hwang, J. Y. ;

Viswanathan, G. B. ;

Tiley, J. ;

Srinivasan, R. ;

Fraser, H. L. ;

Banerjee, R. .

MATERIALS CHARACTERIZATION, 2011, 62 (09) :878-886

[16] Influence of aging heat treatment on microstructure and hardness of single crystal Ni3Al-base superalloy IC21 [J].

Wei, Li ;

Zhang, Zhigang ;

Zhang, Heng ;

Li, Shusuo ;

Gong, Shengkai .

2011 CHINESE MATERIALS CONFERENCE, 2012, 27 :1081-1088

[17] Morphological instability of spherical γ′ precipitates in a nickel base superalloy [J].

Yoo, YS .

SCRIPTA MATERIALIA, 2005, 53 (01) :81-85

← 1 2 →