The effect of long-term thermal exposures on the microstructure and properties of CMSX-10 single crystal Ni-base superalloys

被引：244
作者：
Acharya, A [1 ]
Fuchs, GE [1 ]
机构：
[1] Univ Florida, Dept Mat Sci & Engn, Gainesville, FL 32611 USA
来源：
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2004年 / 381卷 / 1-2期
基金：
美国国家科学基金会;
关键词：
Ni-base superalloy; single crystal; microstructural stability;
D O I：
10.1016/j.msea.2004.04.001
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The long-term thermal stability of CMSX-10 single crystal superalloys has been studied as a function of heat treatment and thermal exposure. The CMSX-10 alloys were subjected to long-term unstressed heat treatments at temperatures of 950 and 1050degreesC for periods of 1000 and 10.000 h. The microstructures and creep properties of the samples before and after long-term thermal exposures were characterized. The gamma' coarsening was observed after all exposures and the formation of topologically close packed (TCP) phases was observed in both samples exposed at 1050 degreesC and the 10 kh exposure at 950 degreesC. High temperature creep tests were carried on these samples at 950 degreesC at an engineering stress of 310 MPa. The creep lives were found to deteriorate with the increase in exposure time and temperature as a result of the microstructural degradation. The coarsening of the gamma' precipitates was observed to be the main factor in the degradation of the properties. (C) 2004 Elsevier B.V. All rights reserved.
引用
收藏
页码：143 / 153
页数：11
相关论文
共 15 条
  • [1] PRECIPITATION HARDENING
    ARDELL, AJ
    [J]. METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1985, 16 (12): : 2131 - 2165
  • [2] CHEN G, 1980, SUPERALLOYS 1980, P355
  • [3] Darolia R., 1988, Superalloys, V1988, P255, DOI DOI 10.7449/1988/SUPERALLOYS_1988_255_264
  • [4] DAVIS JR, 1997, ASM SPECIALTY HDB, P229
  • [5] Duhl D.N., 1987, Superalloys II, VII, P189
  • [6] Erickson GL, 1996, SUPERALLOYS 1996, P35
  • [7] ERICKSON GL, 1995, JOM-J MIN MET MAT S, V47, P36
  • [8] ERICKSON GL, 1995, 2 PAC RIM INT C ADV
  • [9] Improvement of creep strength of a third generation, single-crystal Ni-base superalloy by solution heat treatment
    Fuchs G.E.
    [J]. Journal of Materials Engineering and Performance, 2002, 11 (01) : 19 - 25
  • [10] Solution heat treatment response of a third generation single crystal Ni-base superalloy
    Fuchs, GE
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2001, 300 (1-2): : 52 - 60
12