Fabrication and properties of plasma-sprayed Al2O3/TiO2 composite coatings: A role of nano-sized TiO2 addition

被引：85

作者：

Dejang, N. ^{[1
]}

Watcharapasorn, A. ^{[1
]}

Wirojupatump, S. ^{[2
]}

Niranatlumpong, P. ^{[3
]}

Jiansirisomboon, S. ^{[1
]}

机构：

[1] Chiang Mai Univ, Dept Phys & Mat Sci, Fac Sci, Chiang Mai 50200, Thailand

[2] Chiang Mai Univ, Dept Chem, Fac Sci, Chiang Mai 50200, Thailand

[3] Natl Met & Mat Technol Ctr, Pathum Thani 12121, Thailand

来源：

SURFACE & COATINGS TECHNOLOGY | 2010年 / 204卷 / 9-10期

关键词：

Al2O3/TiO2; Composite; Plasma spraying; Phase; Mechanical properties; Wear; TITANIA COATINGS; MICROSTRUCTURE; BEHAVIOR; POWDERS; ALUMINA;

D O I：

10.1016/j.surfcoat.2009.10.052

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Al2O3/xTiO(2) (where x = 0, 3, 13 and 20 wt%) composite coatings were deposited onto mild steel substrates by atmospheric plasma spraying of mixed micron-sized Al2O3 and nano-sized TiO2 powders. Phase transformation from mainly stable alpha-Al2O3 and anatase-TiO2 in the powders to predominant metastable gamma-Al2O3 and rutile-TiO2 in the coatings was observed. Reaction between Al2O3 and TiO2 phase also occurred producing Al2TiO5 phase. Microstructural investigation showed that well separated TiO2 lamellas were homogeneously dispersed between Al2O3 lamellas. Hardness was found to decrease with increasing TiO2 content while fracture toughness increased. The average wear rates of composite coatings determined by sliding wear test were lower than that of monolithic Al2O3 coating by approximately 40%. This was mainly attributed to an increase in fracture toughness and reduction of friction coefficient due to a presence of TiO2 splats. (C) 2009 Elsevier B.V. All rights reserved.

引用

页码：1651 / 1657

页数：7

共 17 条

[1] MICROSTRUCTURAL DESIGN OF TOUGHENED CERAMICS [J].

BECHER, PF .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1991, 74 (02) :255-269

[2]

Czanderna A.W., 1958, T FARADAY SOC, V54, P1067

[3] PLASMA-SPRAYED WEAR-RESISTANT CERAMIC AND CERMET COATING MATERIALS [J].

DING, CX ;

HUANG, BT ;

LIN, HL .

THIN SOLID FILMS, 1984, 118 (04) :485-493

[4] Tribological behavior of plasma sprayed Al2O3-based cermet coatings [J].

Fervel, V ;

Normand, B ;

Coddet, C .

WEAR, 1999, 230 (01) :70-77

[5] Development and implementation of plasma sprayed nanostructured ceramic coatings [J].

Gell, M ;

Jordan, EH ;

Sohn, YH ;

Goberman, D ;

Shaw, L ;

Xiao, TD .

SURFACE & COATINGS TECHNOLOGY, 2001, 146 :48-54

[6] Microstructure development of Al2O3-13wt.%TiO2 plasma sprayed coatings derived from nanocrystalline powders [J].

Goberman, D ;

Sohn, YH ;

Shaw, L ;

Jordan, E ;

Gell, M .

ACTA MATERIALIA, 2002, 50 (05) :1141-1152

[7] CRITICAL MICROSTRUCTURES FOR MICROCRACKING IN AL2O3-ZRO2 COMPOSITES [J].

GREEN, DJ .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1982, 65 (12) :610-614

[8] Fabrication and evaluation of plasma sprayed nanostructured alumina-titania coatings with superior properties [J].

Jordan, EH ;

Gell, M ;

Sohn, YH ;

Goberman, D ;

Shaw, L ;

Jiang, S ;

Wang, M ;

Xiao, TD ;

Wang, Y ;

Strutt, P .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2001, 301 (01) :80-89

[9] THE QUENCHING STRESS IN THERMALLY SPRAYED COATINGS [J].

KURODA, S ;

CLYNE, TW .

THIN SOLID FILMS, 1991, 200 (01) :49-66

[10] EFFECT OF MICROSTRUCTURE ON STRENGTH OF SI3N4-SIC COMPOSITE SYSTEM [J].

LANGE, FF .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1973, 56 (09) :445-450

← 1 2 →