Study on the effect of carbon nanotube on the properties of electrically conductive epoxy/polyaniline adhesives

被引:18
作者
Khandelwal, Vinay [1 ]
Sahoo, Sushanta K. [1 ]
Kumar, Ashok [2 ]
Manik, Gaurav [1 ]
机构
[1] IIT Roorkee, Dept Polymer & Proc Engn, Saharanpur Campus, Saharanpur 247001, India
[2] CSIR, Natl Phys Lab, Dr KS Krishnan Marg, New Delhi 110012, India
关键词
IN-SITU POLYMERIZATION; EPOXY-RESIN; THERMAL-PROPERTIES; COMPOSITES; POLYANILINE; NANOCOMPOSITES; POLYMERS; SILVER; POLYPYRROLE; MORPHOLOGY;
D O I
10.1007/s10854-017-7282-y
中图分类号
TM [电工技术]; TN [电子技术、通信技术];
学科分类号
0808 ; 0809 ;
摘要
Electrically conductive hybrid epoxy (EP) adhesives filled with p-toluenesulfonic acid (PTSA) doped polyaniline (PANI) and carbon nanotubes (CNT) were prepared and their electrical, thermal and morphological properties were investigated. The CNT was incorporated in EP/PANI (1, 3, 5, 7, 10 and 15 wt%) to obtain hybrid composites aiming to achieve better conductivity. Percolation threshold in EP/PANI and EP/CNT binary composites achieved was at around 5% of PANI and 0.2% CNT, respectively. It was observed that the addition of 0.1% CNT in EP/PANI (5%) composites improved the electrical conductivity of composites with a minimal effect on lap shear strength. Differential scanning calorimetry (DSC) studies revealed that while 0.1% CNT addition had an insignificant retardation effect on the curing of EP/PANI (5%), it increased the glass transition temperature (T (g) ) of cured sample significantly. Although, incorporation of PANI increased the thermal stability of epoxy significantly, addition of CNT further enhanced it marginally in the temperature range of 200-400 A degrees C. FT-IR and XRD spectra of PANI/CNT hybrid fillers system showed molecular level interaction and good dispersing ability of CNT with PANI, respectively. Interestingly, morphological studies showed good dispersion of PANI and CNT in epoxy matrix in binary composites as well as in hybrid composites with no phase separation between PANI and CNT. Optical micrographs showed better dispersion of hybrid PANI/CNT filler system within epoxy matrix compared to PANI only.
引用
收藏
页码:14240 / 14251
页数:12
相关论文
共 51 条
[1]  
Bakhshi AK, 2004, J SCI IND RES INDIA, V63, P715
[2]   Thermomechanical behaviors and dielectric properties of polyaniline-doped para-toluene sulfonic acid/epoxy resin composites [J].
Belaabed, Belkacem ;
Wojkiewicz, Jean Luc ;
Lamouri, Saad ;
El Kamchi, Noureddine ;
Redon, Nathalie .
POLYMERS FOR ADVANCED TECHNOLOGIES, 2012, 23 (08) :1194-1201
[3]   Progress in preparation, processing and applications of polyaniline [J].
Bhadra, Sambhu ;
Khastgir, Dipak ;
Singha, Nikhil K. ;
Lee, Joong Hee .
PROGRESS IN POLYMER SCIENCE, 2009, 34 (08) :783-810
[4]   Simultaneous polymerization and crystallization of aniline [J].
Bhat, NV ;
Seshadri, DT ;
Phadke, RS .
SYNTHETIC METALS, 2002, 130 (02) :185-192
[5]  
Choudhary V, 2013, SYNTHESES AND APPLICATIONS OF CARBON NANOTUBES AND THEIR COMPOSITES, P193, DOI 10.5772/52897
[6]   High performance electrically conductive adhesives from functional epoxy, micron silver flakes, micron silver spheres and acidified single wall carbon nanotube for electronic package [J].
Cui, Hui-Wang ;
Kowalczyk, Agnieszka ;
Li, Dong-Sheng ;
Fan, Qiong .
INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2013, 44 :220-225
[7]   Synthesis and Characterization of Polyaniline/Carbon Nanotube Composites [J].
Ghatak, S. ;
Chakraborty, G. ;
Meikap, A. K. ;
Woods, T. ;
Babu, R. ;
Blau, W. J. .
JOURNAL OF APPLIED POLYMER SCIENCE, 2011, 119 (02) :1016-1025
[8]   Ultrasonic preparation of cellulose/Ag/polyaniline conductive composites and its electrical properties [J].
Gou, Hao ;
He, Jingxian ;
Mo, Zunli ;
Zhao, Zhongli .
JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2015, 26 (09) :7295-7302
[9]   Reinforced magnetic epoxy nanocomposites with conductive polypyrrole nanocoating on nanomagnetite as a coupling agent [J].
Guo, Jiang ;
Zhang, Xi ;
Gu, Hongbo ;
Wang, Yiran ;
Yan, Xingru ;
Ding, Daowei ;
Long, Jun ;
Tadakamalla, Sruthi ;
Wang, Qiang ;
Khan, Mojammel A. ;
Liu, Jingjing ;
Zhang, Xin ;
Weeks, Brandon L. ;
Sun, Luyi ;
Young, David P. ;
Wei, Suying ;
Guo, Zhanhu .
RSC ADVANCES, 2014, 4 (69) :36560-36572
[10]   Polymerization of aniline in the presence of DBSA in an aqueous dispersion [J].
Haba, Y ;
Segal, E ;
Narkis, M ;
Titelman, GI ;
Siegmann, A .
SYNTHETIC METALS, 1999, 106 (01) :59-66