Lithiated nickel oxide electrode performance in molten K2S2O7/V2O5 and K2SO4/V2O5 systems

被引：5
|
作者：
Schmidt, DS [1 ]
McHenry, D [1 ]
Winnick, J [1 ]
机构：
[1] Georgia Inst Technol, Sch Chem Engn, Atlanta, GA 30332 USA
来源：
JOURNAL OF THE ELECTROCHEMICAL SOCIETY | 1998年 / 145卷 / 03期
关键词：
D O I：
10.1149/1.1838363
中图分类号：
O646 [电化学、电解、磁化学];
学科分类号：
081704 ;
摘要：
Lithiated nickel oxide (LixNiyO) electrodes have been successfully used with molten K2S2O7/V2O5 at 400 degrees C and K2SO4/V2O5 at 480 and 520 degrees C in the electrochemical membrane removal of sulfur oxides from simulated flue gases,The porous gas-diffusion electrodes manufactured in the laboratory from commercial Ni electrode material remained stable and conductive in this environment for periods up to 40 days. Polarizations are reported in these systems for current densities up to 50 mA/cm(2). The results show exchange current densities from 0.113 mA/cm(2) at 400 degrees C to 0.8 mA/cm(2) at 520 degrees C.
引用
收藏
页码：892 / 897
页数：6
相关论文
共 50 条
  • [41] K2O-V2O5-AL2O3 AND K2O-V2O5-ZRO2 SYSTEMS
    ABANIN, VI
    FEDOROV, AA
    FOTIEV, AA
    ZHURNAL NEORGANICHESKOI KHIMII, 1986, 31 (12): : 3194 - 3196
  • [42] Structure and dynamical properties of molten V2O5
    Takeda, S
    Kawakita, Y
    Inui, M
    Maruyama, K
    Tamaki, S
    Sugiyama, K
    Waseda, Y
    JOURNAL OF NON-CRYSTALLINE SOLIDS, 1996, 205 (pt 1) : 151 - 154
  • [43] Effects of neodymium oxide on electrochemical properties of V2O5 cathodes for Li/V2O5 secondary batteries
    Zhang, Y
    Hu, XG
    Liu, YW
    Cheng, YS
    ELECTROCHEMICAL AND SOLID STATE LETTERS, 2005, 8 (12) : A633 - A636
  • [44] *O STRUKTURE ZOLEI V2O5
    BERESTNEVA, ZY
    KORETSKAYA, TA
    KARGIN, VA
    DOKLADY AKADEMII NAUK SSSR, 1948, 59 (06): : 1121 - 1124
  • [45] ETCHING OF AL2O3 SURFACES WITH MOLTEN V2O5
    SAFDAR, M
    FRISCHAT, GH
    SALGE, H
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1974, 57 (02) : 106 - 106
  • [46] PHASE-EQUILIBRIA IN MGO-K2O(FE2O3)-V2O5 SYSTEMS
    TUGOVA, NP
    SLOBODIN, BV
    ZHURNAL NEORGANICHESKOI KHIMII, 1983, 28 (05): : 1345 - 1347
  • [47] Temperature sensitive crystallization of V2O5: from amorphous film to β-V2O5 nanorods
    Zou, C. W.
    Yan, X. D.
    Patterson, D. A.
    Emanuelsson, E. A. C.
    Bian, J. M.
    Gao, W.
    CRYSTENGCOMM, 2010, 12 (03): : 691 - 693
  • [48] V2O5在硅胶表面的分散及助剂K2SO4作用的研究
    赵璧英
    王秋霞
    唐有祺
    物理化学学报, 1993, (02) : 187 - 192
  • [49] DETERMINATION OF THE EXPOSED SURFACE-AREA OF V2O5 ON A V2O5/AL2O3 CATALYST
    SOBALIK, Z
    POUR, V
    SOKOLOVA, LA
    NEVSKAYA, OV
    POPOVA, NM
    REACTION KINETICS AND CATALYSIS LETTERS, 1986, 30 (01): : 179 - 184
  • [50] Tribological Properties of Reactive Magnetron Sputtered V2O5 and VN–V2O5 Coatings
    N. Fateh
    G. A. Fontalvo
    C. Mitterer
    Tribology Letters, 2008, 30 : 21 - 26
12345