Lithiated nickel oxide electrode performance in molten K2S2O7/V2O5 and K2SO4/V2O5 systems

被引：5
|
作者：
Schmidt, DS [1 ]
McHenry, D [1 ]
Winnick, J [1 ]
机构：
[1] Georgia Inst Technol, Sch Chem Engn, Atlanta, GA 30332 USA
来源：
JOURNAL OF THE ELECTROCHEMICAL SOCIETY | 1998年 / 145卷 / 03期
关键词：
D O I：
10.1149/1.1838363
中图分类号：
O646 [电化学、电解、磁化学];
学科分类号：
081704 ;
摘要：
Lithiated nickel oxide (LixNiyO) electrodes have been successfully used with molten K2S2O7/V2O5 at 400 degrees C and K2SO4/V2O5 at 480 and 520 degrees C in the electrochemical membrane removal of sulfur oxides from simulated flue gases,The porous gas-diffusion electrodes manufactured in the laboratory from commercial Ni electrode material remained stable and conductive in this environment for periods up to 40 days. Polarizations are reported in these systems for current densities up to 50 mA/cm(2). The results show exchange current densities from 0.113 mA/cm(2) at 400 degrees C to 0.8 mA/cm(2) at 520 degrees C.
引用
收藏
页码：892 / 897
页数：6
相关论文
共 50 条
  • [1] Lithiated nickel oxide electrode performance in molten K2S2O7/V2O5 and K2SO4/V2O5 systems
    Georgia Inst of Technology, Atlanta, United States
    J Electrochem Soc, 3 (892-897):
  • [2] Molten V2O5/Cs0.9K0.9Na0.2S2O7 and V2O5/K2S2O7 catalysts as electrolytesin an electrocatalytic membrane separation device for SO2 removal
    Rasmussen, SB
    Eriksen, KM
    Fehrmann, R
    Winnick, J
    JOURNAL OF APPLIED ELECTROCHEMISTRY, 2002, 32 (01) : 19 - 23
  • [3] Molten V2O5/Cs0.9K0.9Na0.2S2O7 and V2O5/K2S2O7 catalysts as electrolytesin an electrocatalytic membrane separation device for SO2 removal
    S.B. Rasmussen
    K.M. Eriksen
    R. Fehrmann
    J. Winnick
    Journal of Applied Electrochemistry, 2002, 32 : 19 - 23
  • [4] DUAL REACTOR INVESTIGATION OF SO2-OXIDATION WITH A V2O5/K2S2O7 CATALYST
    SORENSEN, JL
    LIVBJERG, H
    VILLADSEN, J
    CHEMICAL ENGINEERING SCIENCE, 1988, 43 (08) : 2269 - 2274
  • [5] Hot corrosion behavior of NdYbZr2O7 exposed to V2O5 and Na2SO4 + V2O5 molten salts
    Wu, Yang
    Bai, Zhiming
    Zheng, Lei
    He, Wenting
    Guo, Hongbo
    CERAMICS INTERNATIONAL, 2020, 46 (07) : 8543 - 8552
  • [6] EPR study of RLi2O V2O5, RNa2O V2O5, RCaO V2O5, and RBaO V2O5 modified vanadate glass systems
    McKnight, J. M.
    Whitmore, K. A.
    Bunton, P. H.
    Baker, D. B.
    Vennerberg, D. C.
    Feller, S. A.
    JOURNAL OF NON-CRYSTALLINE SOLIDS, 2010, 356 (43) : 2268 - 2272
  • [7] THE ELECTROCHEMISTRY OF MOLTEN K2S2O7+K2SO4+V2O5 ELECTROLYTES
    FRANKE, M
    WINNICK, J
    JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 1987, 238 (1-2): : 163 - 182
  • [8] The characterization of nanocrystalline V2O5 and mixed V2O5/Ce oxide
    Orel, ZC
    Kuscer, D
    Kosec, M
    Turkovic, A
    SURFACE AND COLLOID SCIENCE, 2004, 128 : 120 - 125
  • [9] STUDY ON DISPERSION OF V2O5 ON SURFACE OF SiO2 AND THE EFFECT OF PROMOTER K2SO4
    Zhao Biying
    Wang Qiuxia
    Tang Youqi
    ACTA PHYSICO-CHIMICA SINICA, 1993, 9 (02) : 187 - 192
  • [10] EFFECT OF V2O5 ON SYSTEM K2SO4-SO3
    PENFOLD, D
    JOURNAL OF THE INSTITUTE OF FUEL, 1970, 43 (352): : 151 - &
12345