EFFECT OF METALLURGICAL PARAMETERS ON THE PERFORMANCE OF Al-2%Cu-BASED ALLOYS

被引:7
作者
Zaki, G. A. [1 ]
Samuel, A. M. [1 ]
Samuel, F. H. [1 ]
Doty, H. W. [2 ]
机构
[1] Univ Quebec Chicoutimi, Chicoutimi, PQ, Canada
[2] Gen Motors, Mat Engn, Pontiac, MI USA
关键词
aluminum alloys; heat treatment; casting technology; tensile properties; grain structure; HOT-TEARING SUSCEPTIBILITY; MECHANICAL-PROPERTIES; GRAIN REFINER; OMEGA-PHASE; TI-B; SI; MICROSTRUCTURE; TENSILE; ZR; TEMPERATURE;
D O I
10.1007/s40962-016-0113-8
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
The present study was performed on a recently developed Al-Cu alloy, designed for automotive applications. This alloy has the composition Al-2%Cu-1.32%Si-0.42%Mg-0.58%Fe-0.59%Mn-0.07%Ti. It was determined that the alloy containing (0.5% Zr + 0.15% Ti) was the most effective in maximizing the alloy tensile strength over the range of aging temperatures studied, from 155 to 300 degrees C. The addition of Ag is beneficial at high aging temperatures, in the range of 240-300 degrees C when added simultaneously with 0.27 wt% Zr. However, it is less effective when compared to a high Zr concentration (about 0.62 wt%) at the same levels of Ti. It is concluded that the alloy tensile properties may be determined by contributions from different strengthening mechanisms, namely the grain size, the volume fraction of intermetallics produced, and evolution and growth of the hardening precipitates with respect to the aging conditions. Quality charts constructed from the tensile data may be used to select the appropriate metallurgical conditions for tailoring the alloy properties to those required for a specific application. Increasing the copper content from 2 to 3.5 wt% does not produce a significant increase in the alloy strength. However, it increases the calculated alloy density from approximately 2.78 to 2.93 g/cm(3).
引用
收藏
页码:581 / 597
页数:17
相关论文
共 31 条
[1]  
[Anonymous], THESIS
[2]  
Caceres C.H., 2001, Journal of Light Metals, V1, P51, DOI DOI 10.1016/S1471-5317(00)00006-7
[3]   Mechanical properties of intermetallic phases in multi-component Al-Si alloys using nanoindentation [J].
Chen, C. -L. ;
Richter, A. ;
Thomson, R. C. .
INTERMETALLICS, 2009, 17 (08) :634-641
[4]  
Chu Y.L., 1993, NADCA Transactions, P361
[5]  
Crepeau P.N., 1995, AFS T, V103, P361
[6]  
DROUZY M, 1980, INT CAST MET J, V5, P43
[7]   DEVELOPMENT OF NEW AL-CU BASED ALLOYS AIMED AT IMPROVING THE MACHINABILITY OF AUTOMOTIVE CASTINGS [J].
Elgallad, E. ;
Samuel, F. ;
Samuel, A. ;
Doty, H. .
INTERNATIONAL JOURNAL OF METALCASTING, 2009, 3 (02) :29-41
[8]   Decomposition of supersaturated solid solutions in Al-Cu-Mg-Si alloys [J].
Eskin, DG .
JOURNAL OF MATERIALS SCIENCE, 2003, 38 (02) :279-290
[9]   PRECIPITATION OF THE OMEGA-PHASE IN AN AL-4.0CU-0.5MG ALLOY [J].
GARG, A ;
CHANG, YC ;
HOWE, JM .
SCRIPTA METALLURGICA ET MATERIALIA, 1990, 24 (04) :677-680
[10]   Optimizing the tensile properties of Al-Si-Cu-Mg 319-type alloys: Role of solution heat treatment [J].
Han, Y. ;
Samuel, A. M. ;
Doty, H. W. ;
Valtierra, S. ;
Samuel, F. H. .
MATERIALS & DESIGN, 2014, 58 :426-438