Decomposition behavior of MGH2 prepared by reaction ball-milling

被引：32

作者：

Wang, P ^{[1
]}

Wang, AM ^{[1
]}

Wang, YL ^{[1
]}

Zhang, HF ^{[1
]}

Hu, ZQ ^{[1
]}

机构：

[1] Chinese Acad Sci, Met Res Inst, State Key Lab RSA, Shenyang 110015, Peoples R China

来源：

SCRIPTA MATERIALIA | 2000年 / 43卷 / 01期

基金：

中国国家自然科学基金;

关键词：

hydrides; composites; reaction ball-milling;

D O I：

10.1016/S1359-6462(00)00370-5

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Mg can be directly hydrided into MgH2 and γ-MgH2 under the action of catalyst ZrFe1.4Cr0.6 by reaction ball milling. The increase of hydrogen content, depending on the grinding time, does not affect the thermodynamic property of the formed hydride. The hydrided phases posses markedly improved desorption kinetics, even at 513 K the decomposition could proceed at moderate rate. According to the analyzing result of local Avrami exponent, it was found that the nucleation was only rate-dominant in the initial decomposition, and then the main reaction mechanism was growth controlled by the diffusion of hydrogen atom. ZrFe1.4Cr0.6 distributing uniformly on the surface and in the bulk matrix, played an important role in accelerating the diffusion of hydrogen atom.

引用

页码：83 / 87

页数：5

共 18 条

[11] Structural and hydriding properties of the Mg-Ni-H system with nano- and/or amorphous structures [J].

Orimo, S ;

Ikeda, K ;

Fujii, H ;

Fujikawa, Y ;

Kitano, Y ;

Yamamoto, K .

ACTA MATERIALIA, 1997, 45 (06) :2271-2278

[12] Recent developments in the applications of nanocrystalline materials to hydrogen technologies [J].

Schulz, R ;

Huot, J ;

Liang, G ;

Boily, S ;

Lalande, G ;

Denis, MC ;

Dodelet, JP .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1999, 267 (02) :240-245

[13] KINETICS OF CRYSTALLIZATION OF AN FE-P-C GLASS [J].

SCOTT, MG ;

RAMACHANDRARAO, P .

MATERIALS SCIENCE AND ENGINEERING, 1977, 29 (02) :137-144

[14] HYDRIDING AND DEHYDRIDING CHARACTERISTICS OF MECHANICALLY ALLOYED MIXTURES MG-5WT.PERCENT-NI, MG-10WT.PERCENT-NI, MG-25WT.PERCENT-NI, MG-55WT.PERCENT-NI [J].

SONG, MY ;

IVANOV, E ;

DARRIET, B ;

PEZAT, M ;

HAGENMULLER, P .

JOURNAL OF THE LESS-COMMON METALS, 1987, 131 :71-79

[15] THE MAGNESIUM HYDROGEN SYSTEM [J].

STAMPFER, JF ;

HOLLEY, CE ;

SUTTLE, JF .

JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 1960, 82 (14) :3504-3508

[16] Hydriding and dehydriding characteristics of Mg-LaNi5 composite materials prepared by mechanical alloying [J].

Terzieva, M ;

Khrussanova, M ;

Peshev, P .

JOURNAL OF ALLOYS AND COMPOUNDS, 1998, 267 (1-2) :235-239

[17]

WANG P, IN PRESS J ALLOYS CO

[18] Nanocrystalline metal hydrides [J].

Zaluski, L ;

Zaluska, A ;

StromOlsen, JO .

JOURNAL OF ALLOYS AND COMPOUNDS, 1997, 253 :70-79

← 1 2 →