Effect of Ti content in Ag-Cu-Ti activated filler metal on dissimilar joint formation of sialon and WC-Co alloy by laser brazing

被引：6
作者：
Nagatsuka, K. [1 ]
Yoshida, S. [1 ]
Sechi, Y. [1 ]
Nakata, K. [1 ]
机构：
[1] Osaka Univ, Joining & Welding Res Inst, Ibaraki, Osaka 5670047, Japan
来源：
SCIENCE AND TECHNOLOGY OF WELDING AND JOINING | 2014年 / 19卷 / 06期
关键词：
Laser brazing; Sialon; WC-Co alloy; Ag-Cu-Ti filler metal; Interface structure; BRAZED JOINTS; MICROSTRUCTURE; STRENGTH; CERAMICS; NITRIDE; STEEL; SI3N4;
D O I：
10.1179/1362171814Y.0000000217
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Laser brazing was carried out for dissimilar joining of sialon and a WC-Co alloy. Eutectic type Ag-Cu alloys as filler metals with different Ti content ranging from 0 to 2.8 mass-% were used to investigate the effects of Ti on the interface structure and strength of the joint. The filler metal sheet was sandwiched between a sialon block and a WC-Co alloy plate, and a laser beam was irradiated selectively on the WC-Co alloy plate. The brazed joint was obtained using the filler metal containing.0.3 mass-% Ti. TiN, Ti5Si3, and Cu4Ti layers were formed at the interface of sialon and brazed metal as compound layers. The shear strength of the brazed joint increased with increasing Ti content in the filler metal in the range 0.3-1.7 mass-%, reaching a maximum value of 106 MPa. However, the strength decreased when the Ti content became higher than 1? 7 mass-%.
引用
收藏
页码：521 / 526
页数：6
相关论文
共 23 条
  • [1] Wetting and reaction between β′-sialon, stainless steel and Cu-Ag brazing alloys containing Ti
    Abed, A
    Jalham, IS
    Hendry, A
    [J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2001, 21 (03) : 283 - 290
  • [2] Microstructure and mechanical properties of Si3N4/Si3N4 joint brazed with Ag-Cu-Ti plus SiCp composite filler
    He, Y. M.
    Zhang, J.
    Liu, C. F.
    Sun, Y.
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2010, 527 (12): : 2819 - 2825
  • [3] Kimura M., 2003, Q J JPN WELD SOC, V21, P448
  • [4] Kimura M., 2002, INT J SOC MAT ENG RE, V10, P81
  • [5] Surface deposits in laser brazing
    Klocke, F.
    Frank, S.
    [J]. SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2013, 18 (01) : 62 - 69
  • [6] A study of the wetting, microstructure and bond strength in brazing SiC by Cu-X(X=Ti,V,Nb,Cr) alloys
    Lee, HK
    Lee, JY
    [J]. JOURNAL OF MATERIALS SCIENCE, 1996, 31 (15) : 4133 - 4140
  • [7] Effect of Ti content on microstructure and strength of Si3N4/Si3N4 joints brazed with Cu-Pd-Ti filler metals
    Liu, C. F.
    Zhang, J.
    Zhou, Y.
    Meng, Q. C.
    Naka, M.
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 491 (1-2): : 483 - 487
  • [8] Improvements of the Si3N4 brazed joints with intermetallics
    Liu, GM
    Zou, GS
    Wu, AP
    Zhang, DK
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 415 (1-2): : 213 - 218
  • [9] Joining of sintered silicon carbide using ternary Ag-Cu-Ti active brazing alloy
    Liu, Y.
    Huang, Z. R.
    Liu, X. J.
    [J]. CERAMICS INTERNATIONAL, 2009, 35 (08) : 3479 - 3484
  • [10] Characteristics of dissimilar laser-brazed joints of isotropic graphite to WC-Co alloy
    Nagatsuka, Kimiaki
    Sechi, Yoshihisa
    Miyamoto, Yoshinari
    Nakata, Kazuhiro
    [J]. MATERIALS SCIENCE AND ENGINEERING B-ADVANCED FUNCTIONAL SOLID-STATE MATERIALS, 2012, 177 (07): : 520 - 523
123