Effect of microstructure of a NiCoCrAlY coating fabricated by high-velocity air fuel on the isothermal oxidation

被引：58

作者：

Lu, Jie ^{[1
]}

Zhang, Han ^{[1
]}

Chen, Ying ^{[2
]}

Zhao, Xiaofeng ^{[1
]}

Guo, Fangwei ^{[1
]}

Xiao, Ping ^{[3
]}

机构：

[1] Shanghai Jiao Tong Univ, Sch Mat Sci & Engn, Shanghai Key Lab Adv High Temp Mat & Precis Formi, Shanghai 200240, Peoples R China

[2] OxMet Technol, Begbroke Sci Pk, Kidlington OX5 1PF, Oxon, England

[3] Univ Manchester, Sch Mat, MSS Tower, Manchester M13 9PL, Lancs, England

来源：

CORROSION SCIENCE | 2019年 / 159卷

基金：

英国工程与自然科学研究理事会;

关键词：

NiCoCrAlY; Grain size; Porosity; Oxidation; THERMAL BARRIER COATINGS; HIGH-TEMPERATURE OXIDATION; MCRALY BOND COATS; NI-AL ALLOYS; CYCLIC OXIDATION; ALUMINA SCALES; RESIDUAL-STRESS; FAILURE; BEHAVIOR; DIFFUSION;

D O I：

10.1016/j.corsci.2019.108126

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The effect of grain size and porosity of a NiCoCrAlY coating fabricated by high-velocity air fuel on the isothermal oxidation behavior is studied. To understand this effect, the microstructure of coating, the chemistry and microstructure of thermally grown oxides (TGO), the phase transformation of alumina, the oxidation rate, and the TGO stress are investigated. It is demonstrated in this study that the oxidation and spallation resistance of TGO are predominantly determined by the porosity rather than grain size for the long term oxidation, although the nanoscale gamma-grains can facilitate the earlier establishment of alpha-Al2O3 scale.

引用

页数：14

共 62 条

[51] THE THERMODYNAMICS OF SPINEL INTERPHASE FORMATION AT DIFFUSION-BONDED NI/AL2O3 INTERFACES [J].

TRUMBLE, KP ;

RUHLE, M .

ACTA METALLURGICA ET MATERIALIA, 1991, 39 (08) :1915-1924

[52] Investigation of TBCs on turbine blades by photoluminescence piezospectroscopy [J].

Wang, X. ;

Lee, G. ;

Atkinson, A. .

ACTA MATERIALIA, 2009, 57 (01) :182-195

[53] Pulsed electron beam treatment of MCrAlY bondcoats for EB PVD TBC systems part 2 of 2: Cyclic oxidation of the coatings [J].

Wellman, R. G. ;

Scrivani, A. ;

Rizzi, G. ;

Weisenburger, A. ;

Tenailleau, F. H. ;

Nicholls, J. R. .

SURFACE & COATINGS TECHNOLOGY, 2007, 202 (4-7) :709-713

[54] Microstructure parameters affecting interfacial adhesion of thermal barrier coatings by the EB-PVD method [J].

Wu, L. T. ;

Wu, R. T. ;

Zhao, X. ;

Xiao, P. .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2014, 594 :193-202

[55] The retention of thermal barrier coating systems on single-crystal superalloys: Effects of substrate composition [J].

Wu, R. T. ;

Kawagishi, K. ;

Harada, H. ;

Reed, R. C. .

ACTA MATERIALIA, 2008, 56 (14) :3622-3629

[56] Observations and analyses of failure mechanisms in thermal barrier systems with two phase bond coats based on NiCoCrAlY [J].

Xu, T ;

Faulhaber, S ;

Mercer, C ;

Maloney, M ;

Evans, A .

ACTA MATERIALIA, 2004, 52 (06) :1439-1450

[57] The influence of platinum on the failure of EBPVD YSZ TBCs on NiCoCrAlY bond coats [J].

Yanar, NM ;

Meier, GH ;

Pettit, FS .

SCRIPTA MATERIALIA, 2002, 46 (04) :325-330

[58] The residual stress of oxide scales grown on Ni-Al alloys doped with minor Dy and Y [J].

Yang, Liyuan ;

Zheng, Lei ;

Guo, Hongbo .

CORROSION SCIENCE, 2016, 112 :542-551

[59] Effects of surface finish on the initial oxidation of HVAF-sprayed NiCoCrAlY coatings [J].

Zhang, Pimin ;

Sadeghimeresht, Esmaeil ;

Chen, Shula ;

Li, Xin-Hai ;

Markocsan, Nicolaie ;

Joshi, Shrikant ;

Chen, Weimin ;

Buyanova, Irina A. ;

Peng, Ru Lin .

SURFACE & COATINGS TECHNOLOGY, 2019, 364 :43-56

[60] Study of oxidation behavior of nanostructured NiCrAlY bond coatings deposited by cold spraying [J].

Zhang, Qiang ;

Li, Chang-Jiu ;

Li, Cheng-Xin ;

Yang, Guan-Jun ;

Lui, Siu-Ching .

SURFACE & COATINGS TECHNOLOGY, 2008, 202 (14) :3378-3384

← 1 2 3 4 5 6 7 →