Effect of microstructure of a NiCoCrAlY coating fabricated by high-velocity air fuel on the isothermal oxidation

被引：58

作者：

Lu, Jie ^{[1
]}

Zhang, Han ^{[1
]}

Chen, Ying ^{[2
]}

Zhao, Xiaofeng ^{[1
]}

Guo, Fangwei ^{[1
]}

Xiao, Ping ^{[3
]}

机构：

[1] Shanghai Jiao Tong Univ, Sch Mat Sci & Engn, Shanghai Key Lab Adv High Temp Mat & Precis Formi, Shanghai 200240, Peoples R China

[2] OxMet Technol, Begbroke Sci Pk, Kidlington OX5 1PF, Oxon, England

[3] Univ Manchester, Sch Mat, MSS Tower, Manchester M13 9PL, Lancs, England

来源：

CORROSION SCIENCE | 2019年 / 159卷

基金：

英国工程与自然科学研究理事会;

关键词：

NiCoCrAlY; Grain size; Porosity; Oxidation; THERMAL BARRIER COATINGS; HIGH-TEMPERATURE OXIDATION; MCRALY BOND COATS; NI-AL ALLOYS; CYCLIC OXIDATION; ALUMINA SCALES; RESIDUAL-STRESS; FAILURE; BEHAVIOR; DIFFUSION;

D O I：

10.1016/j.corsci.2019.108126

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The effect of grain size and porosity of a NiCoCrAlY coating fabricated by high-velocity air fuel on the isothermal oxidation behavior is studied. To understand this effect, the microstructure of coating, the chemistry and microstructure of thermally grown oxides (TGO), the phase transformation of alumina, the oxidation rate, and the TGO stress are investigated. It is demonstrated in this study that the oxidation and spallation resistance of TGO are predominantly determined by the porosity rather than grain size for the long term oxidation, although the nanoscale gamma-grains can facilitate the earlier establishment of alpha-Al2O3 scale.

引用

页数：14

共 62 条

[1] Effects of specimen treatment and surface preparation on the isothermal oxidation behaviour of the HVOF-sprayed MCrA1Y coatings [J].

Brandl, W ;

Marginean, G ;

Maghet, D ;

Utu, D .

SURFACE & COATINGS TECHNOLOGY, 2004, 188 (1-3 SPEC.ISS.) :20-26

[2] The characteristics of alumina scales formed on HVOF-sprayed MCrAlY coatings [J].

Brandl, W ;

Toma, D ;

Grabke, HJ .

SURFACE & COATINGS TECHNOLOGY, 1998, 108 (1-3) :10-15

[3] Effects of breakaway oxidation on local stresses in thermal barrier coatings [J].

Busso, E. P. ;

Evans, H. E. ;

Qian, Z. Q. ;

Taylor, M. P. .

ACTA MATERIALIA, 2010, 58 (04) :1242-1251

[4] Microstructural evolution and failure characteristics of a NiCoCrAlY bond coat in "hot spot" cyclic oxidation [J].

Cao, F. ;

Tryon, B. ;

Torbet, C. J. ;

Pollock, T. M. .

ACTA MATERIALIA, 2009, 57 (13) :3885-3894

[5] Effects of creep-plastic behavior on stress development in TBCs during cooling [J].

Chai, Yijun ;

Lin, Chen ;

Li, Yueming .

CERAMICS INTERNATIONAL, 2017, 43 (15) :11627-11634

[6] Effect of microstructure on early oxidation of MCrAlY coatings [J].

Chen, Ying ;

Zhao, Xiaofeng ;

Xiao, Ping .

ACTA MATERIALIA, 2018, 159 :150-162

[7] PROTECTIVE COATINGS IN THE GAS-TURBINE ENGINE [J].

DEMASIMARCIN, JT ;

GUPTA, DK .

SURFACE & COATINGS TECHNOLOGY, 1994, 68 :1-9

[8] Application of image analysis for characterization of porosity in thermal spray coatings and correlation with small angle neutron scattering [J].

Deshpande, S ;

Kulkarni, A ;

Sampath, S ;

Herman, H .

SURFACE & COATINGS TECHNOLOGY, 2004, 187 (01) :6-16

[9] Effect of high vacuum heat treatment on microstructure and cyclic oxidation resistance of HVOF-CoNiCrAlY coatings [J].

Doolabi, D. Salehi ;

Rahimipour, M. R. ;

Alizadeh, M. ;

Pouladi, S. ;

Hadavi, S. M. M. ;

Vaezi, M. R. .

VACUUM, 2017, 135 :22-33

[10] Mechanisms controlling the durability of thermal barrier coatings [J].

Evans, AG ;

Mumm, DR ;

Hutchinson, JW ;

Meier, GH ;

Pettit, FS .

PROGRESS IN MATERIALS SCIENCE, 2001, 46 (05) :505-553

← 1 2 3 4 5 6 7 →