Preparation and investigation on tetradecanol and myristic acid/cellulose form-stable phase change material

In this paper, a novel form-stable phase change material (FS PCM) was prepared by incorporating the eutectic mixture of tetradecanol (TD) and myristic acid (MA) into the hydroxylpropyl methyl cellulose (HPMC). HPMC is used as support material, and the eutectic mixture is used as phase change material. The Fourier-transform infrared spectroscopy (FT-IR), X-ray diffractometer (XRD) and scanning electron microscopy (SEM) were used to study the chemical structure, crystallization behavior and morphology of the FS PCM, respectively. FT-IR, XRD and SEM showed that the TD-MA was distributed uniformly in HPMC by physical interaction. Specific surface area (BET) and pore size analysis determined the pore characteristics of the composite, and the results showed the porosity of HPMC. The thermal properties, thermal stability and thermal reliability were detected by differential scanning calorimetry (DSC), thermogravimetric analysis (TG), thermal cycling test and leakage test. The TG, DSC and leakage analysis results revealed that the absorption of eutectic mixture into HPMC is nearly 50% and without seepage from the composite. The peak temperatures of melting and solidifying were 34.61 and 31.09 A degrees C, and latent heat was 102.11/84.58 J g(-1) by DSC. TG and cycling experiment detected that the FS PCM showed good thermal stability and reliability performance.