A super-microporous zirconia-alumina nanomaterial with high thermal stability

被引：7
作者：
Li, Yongfeng [1 ]
Su, JiaoJiao [1 ]
Ma, Jinghong [1 ]
Yu, Feng [1 ]
Pan, Dahai [1 ]
Li, Ruifeng [1 ]
机构：
[1] Taiyuan Univ Technol, Coll Chem & Chem Engn, Taiyuan 030024, Peoples R China
来源：
MATERIALS LETTERS | 2014年 / 136卷
基金：
中国国家自然科学基金; 山西省青年科学基金;
关键词：
Super-microporous zirconia-alumina; Large surface area; Thermal stability; MESOPOROUS ALUMINA; FACILE SYNTHESIS; CATALYSTS;
D O I：
10.1016/j.matlet.2014.08.004
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
A super-microporous zirconia-alumina (pore size in the range of 1-2 nm) with narrow pore size distribution has been synthesized successfully by using an inexpensive nonionic surfactant fatty alcohol polyoxyethylene ether (AEO-7) as the template in ethanol solvent. As the Zr/Al molar ratio is 0.1, the material has high surface area of 413 m(2)/g and a large pore volume of 0.17 cm(3)/g after calcination at 400 degrees C. Even after calcination at 900 degrees C, the microporous structure remained, exhibiting a significant thermal stability. (C) 2014 Elsevier B.V. All rights reserved.
引用
收藏
页码：183 / 186
页数：4
相关论文
共 38 条
  • [1] Fabrication of super-microporous nanocrystalline zirconia with high thermal stability
    Su, Jiaojiao
    Li, Yongfeng
    Yan, Xiaoliang
    Li, Ruifeng
    CHEMICAL PHYSICS LETTERS, 2016, 650 : 98 - 101
  • [2] Preparation and characterization of super-microporous alumina with crystalline structure
    Li, Yongfeng
    Su, Jiaojiao
    Li, Ruifeng
    MICROPOROUS AND MESOPOROUS MATERIALS, 2017, 243 : 9 - 15
  • [3] Fabricating mesoporous silica-modified alumina with high thermal stability
    Yuan, Xiaoyan
    Wang, Ruiqin
    Kong, Luo
    Guo, Shouwu
    CHEMICAL PHYSICS LETTERS, 2019, 716 : 126 - 130
  • [4] Improvement of thermal stability of alumina by addition of zirconia
    Horiuchi, T
    Teshima, Y
    Osaki, T
    Sugiyama, T
    Suzuki, K
    Mori, T
    CATALYSIS LETTERS, 1999, 62 (2-4) : 107 - 111
  • [5] Improvement of thermal stability of alumina by addition of zirconia
    Tatsuro Horiuchi
    Yutaka Teshima
    Toshihiko Osaki
    Toyohiko Sugiyama
    Kenzi Suzuki
    Toshiaki Mori
    Catalysis Letters, 1999, 62 : 107 - 111
  • [6] Alumina surface material with high thermal stability
    Li, WX
    Li, DH
    Wang, QW
    LIGHT METALS 2004, 2004, : 143 - 147
  • [7] Thermal Stability of Ferroelectricity in Hafnia-Zirconia-Alumina Buried Oxide Stacks
    Tikhonenko, Fedor
    Antonov, Valentin
    Popov, Vladimir
    Miakonkikh, Andrey
    Rudenko, Konstantin
    2021 JOINT INTERNATIONAL EUROSOI WORKSHOP AND INTERNATIONAL CONFERENCE ON ULTIMATE INTEGRATION ON SILICON (EUROSOI-ULIS), 2021,
  • [8] Amorphous mesostructured zirconia with high (hydro)thermal stability
    Lebeau, Benedicte
    Naboulsi, Issam
    Michelin, Laure
    Marichal, Claire
    Rigolet, Severinne
    Carteret, Cedric
    Brunet, Sylvette
    Bonne, Magali
    Blin, Jean-Luc
    RSC ADVANCES, 2020, 10 (44) : 26165 - 26176
  • [9] Synthesis and characterization of mesoporous Si-modified alumina with high thermal stability
    Xu, Benjing
    Yang, Yang
    Xu, Yanyan
    Han, Baozhai
    Wang, Youhe
    Liu, Xinmei
    Yan, Zifeng
    MICROPOROUS AND MESOPOROUS MATERIALS, 2017, 238 : 84 - 89
  • [10] Alumina-Doped Zirconia Submicro-Particles: Synthesis, Thermal Stability, and Microstructural Characterization
    Dahl, Gregor Thomas
    Doering, Sebastian
    Krekeler, Tobias
    Janssen, Rolf
    Ritter, Martin
    Weller, Horst
    Vossmeyer, Tobias
    MATERIALS, 2019, 12 (18)
1234