Brazing of Inconel 600 by active filler metal

被引：2

作者：

Zaharinie, T. ^{[1
,2
]}

Yusof, F. ^{[1
,2
]}

Hamdi, M. ^{[1
,2
]}

Ariga, T. ^{[3
]}

机构：

[1] Univ Malaya, Dept Mech Engn, Kuala Lumpur, Malaysia

[2] Univ Malaya, AMMP Ctr, Kuala Lumpur, Malaysia

[3] Tokai Univ, Sch Engn, Dept Mat Sci, Hiratsuka, Kanagawa 25912, Japan

来源：

MATERIALS RESEARCH INNOVATIONS | 2014年 / 18卷

关键词：

Brazing; Inconel; 600; Active filler metal; Ag-Cu-Ti; Reaction layer; Shear strength; STAINLESS-STEEL; MECHANICAL-PROPERTIES; TEMPERATURE; ALLOY; MICROSTRUCTURE;

D O I：

10.1179/1432891714Z.000000000968

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Inconel 600 alloy was brazed at three different brazing temperatures 830, 865 and 900 degrees C for 30 minutes. An active filler metal, Ag-Cu-Ti, was utilised to study its effects on bonding strength by the diffusion of some elements with Inconel 600 during brazing. The experiment was carried out in a high vacuum chamber at 1 x 10(-4) Pa. Scanning electron microscope-energy dispersive spectroscopy and electron probe microanalysis was conducted for element identification and a shear test served to evaluate the bonding strength. The results show that good bonding was achieved and two continuous reaction layers were formed in the brazed area. The reaction layers were crossing in the middle in most areas at 865 degrees C compared to 830 and 900 degrees C. It was revealed that a stronger Ti-Ni interaction than Ti-Cu influenced the formation behaviour of reaction layers and the highest shear strength identified was at 865 degrees C.

引用

页码：260 / 263

页数：4

共 50 条

[11] Comparative study on laser brazing and furnace brazing of Inconel 718 alloys with silver based filler metal [J].

Khorram, A. ;

Ghoreishi, M. .

OPTICS AND LASER TECHNOLOGY, 2015, 68 :165-174

[12] Additional active metal Nb in Cu-Ni system filler metal for brazing of TIC cermet/steel [J].

Li, Jia ;

Sheng, Guangmin ;

Huang, Li .

MATERIALS LETTERS, 2015, 156 :10-13

[13] Active brazing filler metal on SiC particle reinforced aluminium matrix composites [J].

Wang, P. ;

Xu, D. X. ;

Cheng, D. F. ;

Li, Q. ;

Niu, J. T. .

SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2015, 20 (05) :361-370

[14] Brazing of SiC ceramics pretreated by chromium coating using inactive AgCu filler metal [J].

Chen, Zubin ;

Hu, Shengpeng ;

Song, Xiaoguo ;

Lei, Yu ;

Wang, Xinyuan ;

Long, Weimin ;

Feng, Jicai .

INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2020, 17 (06) :2591-2597

[15] Influence of sulphur on the microstructure and properties of Ag-Cu-Zn brazing filler metal [J].

Chen, Y. ;

Yun, D. ;

Sui, F. ;

Long, W. ;

Zhang, G. ;

Liu, S. .

MATERIALS SCIENCE AND TECHNOLOGY, 2013, 29 (10) :1267-1271

[16] Wetting and Brazing of Chromium Film-Deposited Alumina Using AgCu Filler Metal [J].

Chen, Z. B. ;

Bian, H. ;

Niu, C. N. ;

Song, X. G. ;

Lei, Y. Z. ;

Jin, C. ;

Cao, J. ;

Feng, J. C. .

JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2018, 27 (10) :5470-5477

[17] Joining alumina to Inconel 600 and UMCo-50 superalloys using an Sn10Ag4Ti active filler metal [J].

S. Y. Chang ;

Y. T. Hung ;

T. H. Chuang .

Journal of Materials Engineering and Performance, 2003, 12 (2) :123-127

[18] Joining alumina to Inconel 600 and UMCo-50 superalloys using an Sn10Ag4Ti active filler metal [J].

Chang, SY ;

Hung, YT ;

Chuang, TH .

JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2003, 12 (02) :123-127

[19] Vacuum brazing of sapphire with Inconel 600 using Cu/Ni porous composite interlayer for gas pressure sensor application [J].

Zaharinie, Tuan ;

Moshwan, Raza ;

Yusof, Farazila ;

Hamdi, M. ;

Ariga, Tadashi .

MATERIALS & DESIGN, 2014, 54 :375-381

[20] Active metal brazing of SiO2-BN ceramic and Ti plate with Ag-Cu-Ti plus BN composite filler [J].

Yang, Z. W. ;

Wang, C. L. ;

Wang, Y. ;

Zhang, L. X. ;

Wang, D. P. ;

Feng, J. C. .

JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2017, 33 (11) :1392-1401

← 1 2 3 4 5 →