Effects of Rapid Thermal Annealing on Ar Inductively Coupled Plasma-Treated n-Type 4H-SiC Schottky and Ohmic Contacts

被引:12
作者
Cheng, Jung-Chien [1 ]
Tsui, Bing-Yue [1 ]
机构
[1] Natl Chiao Tung Univ, Inst Elect, Hsinchu 300, Taiwan
关键词
Inductively coupled plasma (ICP) treatment; ohmic contact; Schottky-barrier diode (SBD); Schottky-barrier height (SBH); silicon carbide (SiC); specific contact resistance; WIDE-BANDGAP SEMICONDUCTOR; SILICON-CARBIDE; POWER DEVICES; DEPOSITION; SI;
D O I
10.1109/TED.2018.2859272
中图分类号
TM [电工技术]; TN [电子技术、通信技术];
学科分类号
0808 ; 0809 ;
摘要
The effects of Ar inductively coupled plasma (ICP) treatment followed by a 600 degrees C-1000 degrees C rapid thermal annealing (RTA) on the n-type 4H-silicon carbide (SiC) Schottky-barrier diodes and n(+)-implanted ohmic contacts were investigated. The ICP treatment created a 3-nm-thick, sp(2)-C-rich, and amorphous layer at the SiC surface. The RTA repaired the bombardment-induced damages before metal deposition to avoid current degradation. This ICP + RTA-treated surface strongly pinned the Schottky- barrier height (SBH) at a minimum of 0.88 eV. In theory, the low SBH is beneficial to decrease the specific contact resistance (rho(C)). rho(C) of the ICP + RTA-treated Ti ohmic contacts decreased to lower than 10(-5) Omega.cm(2) after 400 degrees C post-metal deposition annealing (PMDA). However, the additional O atoms, fixed in the amorphous layer by RTA, affected the rho(C) reduction. Fortunately, due to the chemical affinity for O of Ti, the in-diffused Ti could contend for the O atoms against the Si-O bonds during the PMDA. Therefore, the oxidized barricade was decomposed gradually, leading to the lowest rho(C), 1.3 x 10(-6) Omega.cm(2), after 600 degrees C PMDA. The lowest rho(C) is 25x and 8x lower than that of the Ni silicide and the nontreated Ti contacts, respectively, at the same doping concentration.
引用
收藏
页码:3739 / 3745
页数:7
相关论文
共 36 条
[1]   COMPARISON OF 6H-SIC, 3C-SIC, AND SI FOR POWER DEVICES [J].
BHATNAGAR, M ;
BALIGA, BJ .
IEEE TRANSACTIONS ON ELECTRON DEVICES, 1993, 40 (03) :645-655
[2]   Status of silicon carbide (SiC) as a wide-bandgap semiconductor for high-temperature applications: A review [J].
Casady, JB ;
Johnson, RW .
SOLID-STATE ELECTRONICS, 1996, 39 (10) :1409-1422
[3]   Reduction of Specific Contact Resistance on n-Type Implanted 4H-SiC Through Argon Inductively Coupled Plasma Treatment and Post-Metal Deposition Annealing [J].
Cheng, Jung-Chien ;
Tsui, Bing-Yue .
IEEE ELECTRON DEVICE LETTERS, 2017, 38 (12) :1700-1703
[4]   Strategic Overview of High-Voltage SiC Power Device Development Aiming at Global Energy Savings [J].
Cheng, Lin ;
Palmour, John W. ;
Agarwal, Anant K. ;
Allen, Scott T. ;
Brunt, Edward V. ;
Wang, Gangyao ;
Pala, Vipindas ;
Sung, Woongje ;
Huang, Alex Q. ;
O'Loughlin, Michael ;
Burk, Albert ;
Grider, Dave ;
Scozzie, Charles .
SILICON CARBIDE AND RELATED MATERIALS 2013, PTS 1 AND 2, 2014, 778-780 :1089-+
[5]   WIDE BANDGAP COMPOUND SEMICONDUCTORS FOR SUPERIOR HIGH-VOLTAGE UNIPOLAR POWER DEVICES [J].
CHOW, TP ;
TYAGI, R .
IEEE TRANSACTIONS ON ELECTRON DEVICES, 1994, 41 (08) :1481-1483
[6]  
Crofton J, 1997, PHYS STATUS SOLIDI B, V202, P581, DOI 10.1002/1521-3951(199707)202:1<581::AID-PSSB581>3.0.CO
[7]  
2-M
[8]   Atomic surface structure of graphene and its buffer layer on SiC(0001): A chemical-specific photoelectron diffraction approach [J].
de Lima, L. H. ;
de Siervo, A. ;
Landers, R. ;
Viana, G. A. ;
Goncalves, A. M. B. ;
Lacerda, R. G. ;
Haeberle, P. .
PHYSICAL REVIEW B, 2013, 87 (08)
[9]  
Dev Alok, 1993, International Electron Devices Meeting 1993. Technical Digest (Cat. No.93CH3361-3), P691, DOI 10.1109/IEDM.1993.347218
[10]   X-ray photoelectron spectroscopy (XPS) and diffraction (XPD) study of a few layers of graphene on 6H-SiC(0001) [J].
Ferrah, D. ;
Penuelas, J. ;
Bottela, C. ;
Grenet, G. ;
Ouerghi, A. .
SURFACE SCIENCE, 2013, 615 :47-56