Laser alloying of zinc with aluminum: Solidification behavior

被引：9

作者：

Carvalho, PA ^{[1
]}

Deus, AM ^{[1
]}

Colaco, R ^{[1
]}

Vilar, R ^{[1
]}

机构：

[1] Univ Tecn Lisboa, Dept Mat Engn, Inst Super Tecn, P-1096 Lisbon, Portugal

来源：

ACTA MATERIALIA | 1998年 / 46卷 / 05期

关键词：

D O I：

10.1016/S1359-6454(97)00229-2

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Laser alloyed tracks were produced by blowing aluminum. powder into melt pools generated in zinc substrates. Analysis of the microstructures revealed a structural and compositional stratification related with a deficient aluminum redistribution in the liquid. The effect of chemical heterogeneity on solidification mechanisms was modeled. The composition gradients and the solidification undercooling were shown to strongly influence the geometry of the solidification front. A reasonable agreement was obtained between experimental and predicted characteristic dimensions of the microstructures, in particular, the radii of the dendrite tips observed experimentally were comparable to the calculated ones. (C) 1997 Acta Metallurgica Inc.

引用

页码：1781 / 1792

页数：12

共 38 条

[31]

MUNDRA K, 1992, WELD J, V71, pS313

[32] MICROSTRUCTURE OF RAPIDLY SOLIDIFIED LASER MOLTEN AL-4.5 WT PCT CU SURFACES [J].

MUNITZ, A .

METALLURGICAL TRANSACTIONS B-PROCESS METALLURGY, 1985, 16 (01) :149-161

[33]

Pirch N, 1996, NATO ADV SCI I E-APP, V307, P177

[34]

Smurov I, 1996, NATO ADV SCI I E-APP, V307, P267

[35]

SYNECEK V, 1992, Z METALLKD, V83, P245

[36]

TRIVEDI R, 1994, INT MATER REV, V39, P49, DOI 10.1179/095066094790326220

[37] Microstructural changes in welded Zn-Al alloy [J].

Zhu, YH .

JOURNAL OF MATERIALS RESEARCH, 1996, 11 (03) :593-598

[38]

[No title captured]

← 1 2 3 4 →