A Critical Conception of Hot-Tearing Susceptibility: Shape Casting with Wrought Aluminum Alloys

被引:8
作者
Pourgharibshahi, Mohammad [1 ]
Saghafian, Hassan [2 ]
Divandari, Mehdi [2 ]
Golestannejad, Farrokh [2 ]
机构
[1] Sirjan Univ Technol, Dept Chem & Mat Engn, Sirjan 7813733385, Iran
[2] Iran Univ Sci & Technol, Sch Met & Mat Engn, Tehran 1684613114, Iran
关键词
hot-tearing susceptibility; controlled diffusion solidification; fractography; shape casting; solid feeding; instrumented rod casting; CONTROLLED DIFFUSION SOLIDIFICATION; TENSILE-STRENGTH; GRAIN-REFINEMENT; AL-ALLOYS; CRACKING; NUCLEATION; APPARATUS; PRESSURE; BEHAVIOR;
D O I
10.1007/s40962-021-00632-5
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
Instrumented constrained rod casting method and the controlled diffusion solidification (CDS) process were used to study the high susceptibility of the aluminum alloy AA 7068 to hot tearing. A precise analysis of the measured hot-tearing curves is provided considering the casting design and different feeding mechanisms. Scanning electron microscopy was used to study the hot-tear surfaces. It was found that the solidification of the eutectic liquid at the film stage and the phenomenon of solid feeding strongly affects the hot-tear formation. The early formation of an absorbed eutectic layer on the primary phase due to low rate of back-diffusion is proposed to explain the loss of ductility at the film stage. The layer can serve as an efficient substrate for the eutectic nucleation and growth; hence, its formation can advance the eutectic solidification. The isolation of liquid eutectic by its partial solidification results in development of solid-feeding stresses breaking the solid eutectic and provides the required tearing initiators. By increasing the back-diffusion rate, the CDS process avoids formation of the adsorbed solid layer which postpones eutectic solidification thereby mitigating the hot-tearing susceptibility.
引用
收藏
页码:853 / 870
页数:18
相关论文
共 74 条
[1]   The formation of lamellar-eutectic grains in thin samples [J].
Akamatsu, S ;
Moulinet, S ;
Faivre, G .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2001, 32 (08) :2039-2048
[2]   CDS method for casting aluminum-based wrought alloy compositions:: theoretical framework [J].
Apelian, D. ;
Makhlouf, M. M. ;
Saha, D. .
ALUMINIUM ALLOYS 2006, PTS 1 AND 2: RESEARCH THROUGH INNOVATION AND TECHNOLOGY, 2006, 519-521 :1771-1776
[3]  
Applett WR., 1954, WELD J, V33, P83
[4]   CONTROLLED DIFFUSION SOLIDIFICATION OF 2024, 6082 AND 7075 Al ALLOYS VIA TILT-POUR CASTING PROCESS [J].
Ashtari, P. ;
Birsan, G. ;
Khalaf, A. ;
Shankar, S. .
INTERNATIONAL JOURNAL OF METALCASTING, 2011, 5 (02) :43-64
[5]  
Backerud L., 1986, SOLIDIFICATION CHARA, V1
[6]   Roles of Alloy Composition and Grain Refinement on Hot Tearing Susceptibility of 7xxx Aluminum Alloys [J].
Bai, Q. L. ;
Li, Y. ;
Li, H. X. ;
Du, Q. ;
Zhang, J. S. ;
Zhuang, L. Z. .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2016, 47A (08) :4080-4091
[7]  
Braccini M, 2000, MATE RIAUX TECH, V88, P19, DOI [10.1051/mattech/200088050019, DOI 10.1051/MATTECH/200088050019]
[8]  
Campbell J, 2015, COMPLETE CASTING HANDBOOK: METAL CASTING PROCESSES, METALLURGY, TECHNIQUES AND DESIGN, 2ND EDITION, pCP3
[9]  
CAMPBELL J, 1967, T METALL SOC AIME, V239, P138
[10]   STOP POURING, START CASTING [J].
Campbell, J. .
INTERNATIONAL JOURNAL OF METALCASTING, 2012, 6 (03) :7-18