Study on improving microstructure and mechanical properties of directionally solidified Ti44Al6Nb1Cr alloy by cyclic DHT

被引:11
作者
Chen, Ruirun [1 ,2 ]
Liu, Yangli [1 ]
Xue, Xiang [1 ]
Fang, Hongze [1 ]
Tan, Yingmei [1 ]
Cui, Hongzhi [2 ]
机构
[1] Harbin Inst Technol, Natl Key Lab Precis Hot Proc Met, Harbin 150001, Heilongjiang, Peoples R China
[2] Shandong Univ Sci & Technol, Sch Mat Sci & Engn, Qingdao 266590, Shandong, Peoples R China
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2021年 / 809卷
基金
中国国家自然科学基金; 中国博士后科学基金;
关键词
TiAl alloy; Directional solidification; B2; phase; Columnar grains; Mechanical properties; Heat treatment; HIGH-NB; TIAL ALLOY; PHASE-TRANSFORMATION; TENSILE PROPERTIES; FRACTURE-BEHAVIOR; EVOLUTION;
D O I
10.1016/j.msea.2021.140912
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
To improve microstructure of high-Nb TiAl alloys after directional solidification (DS) further, DS Ti44Al6Nb1Cr alloy was conducted cyclic directional heat treatment (DHT) for 1 and 4 times under pulling rate of 4.17 mu m/s at 1750 K, respectively. Results indicate that columnar grains grow up obviously after DHT. Compared with DS alloy (2.56 mm), the maximum width of columnar grains is up to about 9.07 mm for DHT alloy after 4 times (DHT-4). The SEM images and EDS results indicate that phase component of DS alloy has not changed after cyclic DHT for different times. It is still composed of alpha(2), gamma and B2 phases. As cyclic DHT times increase, thickness of lamellar phases increases gradually. More massive gamma phases precipitate from B2 phases and grow up. The content of B2 phases reduces due to atoms diffusing sufficiently during cyclic DHT. Tensile curves show optimal mechanical properties are obtained in DHT alloy for 1 time (DHT-1). The ultimate tensile strength is 636 MPa and total strain is 2.28%. Compared with that of DS alloy (523 MPa and 3.03%), tensile strength is improved greatly. As cyclic times increase, mechanical properties decrease for DHT alloy, due to massive. phases coarsening and B2 phases distributing discontinuously. This microstructure could not hinder cracks propagation effectively, which may be the main reasons to result in premature fracture for DHT-4 alloy. At 973 K, the better mechanical properties are still achieved in DHT-1 alloy. The ultimate tensile strength is up to 695 MPa and total strain is 6.21%. The mechanical properties improvement is mainly resulted from directional microstructure, especially the directional lamellar clusters and B2 phases. In addition, dislocations, stacking fault bands and deformation twins are observed in lamellar gamma phases of DHT-1 alloy. These microstructure changes play an important role in improving compressive mechanical properties of DHT alloy.
引用
收藏
页数:9
相关论文
共 29 条
[1]  
Blackburn MJ., 1970, SCI TECHNOLOGY APPL, P633, DOI [10.1016/B978-0-08-006564-9.50071-3, DOI 10.1016/B978-0-08-006564-9.50071-3]
[2]   Research Progress on Controlled Solidification and Its Applications [J].
Chen Guang ;
Zheng Gong ;
Qi Zhixiang ;
Zhang Jinpeng ;
Li Pei ;
Cheng Jialin ;
Zhang Zhongwu .
ACTA METALLURGICA SINICA, 2018, 54 (05) :669-681
[3]  
Chen G, 2016, NAT MATER, V15, P876, DOI [10.1038/nmat4677, 10.1038/NMAT4677]
[4]   Microstructure refinement via martensitic transformation in TiAl alloys [J].
Chen, Lin ;
Lin, Junpin ;
Xu, Xiangjun ;
Li, Chan ;
Xu, Yong ;
Liang, Yongfeng .
JOURNAL OF ALLOYS AND COMPOUNDS, 2018, 741 :1175-1182
[5]   Investigation of macro/microstructure evolution and mechanical properties of directionally solidified high-Nb TiAl-based alloy [J].
Chen, Ruirun ;
Dong, Shulin ;
Guo, Jingjie ;
Ding, Hongsheng ;
Su, Yanqing ;
Fu, Hengzhi .
MATERIALS & DESIGN, 2016, 89 :492-506
[6]   Microstructure evolution and mechanical properties of directionally-solidified TiAlNb alloy in different temperature gradients [J].
Chen, Ruirun ;
Dong, Shulin ;
Guo, Jingjie ;
Ding, Hongsheng ;
Su, Yanqing ;
Fu, Hengzhi .
JOURNAL OF ALLOYS AND COMPOUNDS, 2015, 648 :667-675
[7]   Effect of heat-treatment on the microstructure and fatigue properties of lamellar γ-TiAl alloyed with Nb, Mo and/or C [J].
Chlupova, Alice ;
Heczko, Milan ;
Obrtlik, Karel ;
Dlouhy, Antonin ;
Kruml, Tomas .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2020, 786
[8]   Characterization of the elevated temperature compressive deformation behavior of high Nb containing TiAl alloys with two microstructures [J].
Chu, Yudong ;
Li, Jinshan ;
Zhao, Fengtong ;
Tang, Bin ;
Kou, Hongchao .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2018, 725 :466-478
[9]   Effect of growth rate on microstructure and tensile properties of Ti-45Al-2Cr-2Nb prepared by electromagnetic cold crucible directional solidification [J].
Ding, Hongsheng ;
Wang, Yongzhe ;
Chen, Ruirun ;
Guo, Jingjie ;
Fu, Hengzhi .
MATERIALS & DESIGN, 2015, 86 :670-678
[10]   Directional solidification of TiAl-W-Si alloy by electromagnetic confinement of melt in cold crucible [J].
Ding, Hongsheng ;
Nie, Ge ;
Chen, Ruirun ;
Guo, Jingjie ;
Fu, Hengzhi .
INTERMETALLICS, 2012, 31 :264-273