Friction stir lap welds of AA6111 aluminum alloy

被引：0
|
作者：
Yadava, M. [1 ]
Mishra, R. S. [1 ]
Chen, Y. L. [1 ]
Gayden, X. Q. [1 ]
Grant, G. J. [1 ]
机构：
[1] Univ Missouri, Ctr Frict Stir Proc Mat Sci & Engn, Rolla, MO 65401 USA
来源：
FRICTION STIR WELDING AND PROCESSING IV | 2007年
关键词：
lap joints; AA6111; lap shear tests; effective thickness; hooking defect;
D O I：
暂无
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Lap joints of I mm thick AA6111 aluminum sheets were made by friction stir welding, using robotic and conventional machines. Welds were made for advancing as well as retreating side loading. Thinning in welds was quantified. Lap shear test of welds was conducted in as-welded and paint-baked conditions. Paint bake treatment improved the weld strength; but the improvement varied with process parameters. Advancing side loaded welds achieved higher strength than the retreating side loaded welds. Fracture was found to occur on the loaded side of the weld and along the thinning defect.
引用
收藏
页码：203 / +
页数：2
相关论文
共 50 条
  • [1] CONSTITUTIVE EQUATIONS OF AA6111 ALUMINUM ALLOY
    Wang, B. Z.
    Huang, X. M.
    Wang, C.
    Wang, Z. Y.
    Xing, C.
    Ji, H. C.
    METALURGIJA, 2019, 58 (3-4): : 267 - 271
  • [2] Precipitation strengthening of the aluminum alloy AA6111
    Wang, X
    Poole, WJ
    Esmaeili, S
    Lloyd, DJ
    Embury, JD
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2003, 34A (12): : 2913 - 2924
  • [3] Precipitation strengthening of the aluminum alloy AA6111
    X. Wang
    J. D. Embury
    W. J. Poole
    S. Esmaeili
    D. J. Lloyd
    Metallurgical and Materials Transactions A, 2003, 34 : 2913 - 2924
  • [4] Development of roping in an aluminum automotive alloy AA6111
    Baczynski, GJ
    Guzzo, R
    Ball, MD
    Lloyd, DJ
    ACTA MATERIALIA, 2000, 48 (13) : 3361 - 3376
  • [5] On the thermodynamic stability of intermetallic phases in the AA6111 aluminum alloy
    Abou Khatwa, MK
    Malakhov, DV
    CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 2006, 30 (02): : 159 - 170
  • [6] Microstructures and fatigue properties of friction stir lap welds in aluminum alloy AA6061-T6
    Xu, Xiaodong
    Yang, Xinqi
    Zhou, Guang
    Tong, Jianhua
    MATERIALS & DESIGN, 2012, 35 : 175 - 183
  • [7] Tensile Properties of Friction Stir Welds of AA 7020 Aluminum Alloy
    Akbar Heidarzadeh
    Reza Vatankhah Barenji
    Mohsen Esmaily
    Atabak Rahimzadeh Ilkhichi
    Transactions of the Indian Institute of Metals, 2015, 68 : 757 - 767
  • [8] Tensile Properties of Friction Stir Welds of AA 7020 Aluminum Alloy
    Heidarzadeh, Akbar
    Barenji, Reza Vatankhah
    Esmaily, Mohsen
    Ilkhichi, Atabak Rahimzadeh
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2015, 68 (05) : 757 - 767
  • [9] Strengthening characteristics of AA6111 aluminum
    Quainoo, GK
    Yannacopoulos, S
    Gupta, AK
    CANADIAN METALLURGICAL QUARTERLY, 2001, 40 (02) : 211 - 219
  • [10] The Microstructural Evolution of AA6111 Aluminum Alloy during Homogenization Treatment
    Zhang, Shijiao
    Xiong, Baiqing
    Zhang, Yongan
    Li, Xiwu
    Wang, Feng
    Li, Zhihui
    Liug, Hongwei
    MATERIALS PERFORMANCE, MODELING AND SIMULATION, 2013, 749 : 223 - 228
12345